Electronics Forum | Fri May 07 18:02:37 EDT 1999 | Bill Schreiber
Just a note about cleaning SMD adhesives. Cleaning does not need to be hazardous. Smart Sonic has a non hazardous process that has been used for over 9 years using a non hazardous detergent that has been certified by the AQMD as a clean air chemist
Electronics Forum | Tue Oct 06 17:17:44 EDT 1998 | Chrys
| We are experiencing poor wetting on various components placed on a PCB with En-Tek coating. Is anyone else experiencing simular problems ? We have the following questions: | | 1. How can the thickness of the En-tek coating be measured? | 2. Is En
Electronics Forum | Mon Sep 28 10:12:53 EDT 1998 | Chrys
| Hello, | I need some users information about "Air knif" in wave soldering: | 1. Does it decreases bridging ? | 2. Is it self installed of a purchesed kit (if purchesed, who are the recomended vendors) ? | 3. Any other information about the issue. |
Electronics Forum | Fri Aug 21 07:57:20 EDT 1998 | Earl Moon
| | | Will somebody please explain HASL (here). Thanks. | | Tryin: HASL: Hot Air Solder Leveled. A board fabrication process that applies an oxidation preventing solder coating to copper pads on the board. Dave F | You do this to keep the green s
Electronics Forum | Mon Aug 17 02:57:47 EDT 1998 | Bob Willis
| | Looking for Suppliers of surface mount wetting balance equipment. | Bucky: Section 6 of the ANSI/J-STD-002 specification lists wetting balance suppliers. Dave F I like and continue to use the Multicore system. I have had many ours using the sys
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Tue Apr 14 15:50:45 EDT 1998 | Bob Barr
Justin, Thanks for the response to my dilemma. For once it's not just me! The parts seem perfectly solderable, but I will try the modification to the profile you suggested. I wonder if the retention clips may be letting loose from the holes they a
Electronics Forum | Tue Mar 10 22:16:56 EST 1998 | Steve Gregory
Jeremy, I'm gonna make a couple of assumptions by "reading in between the lines" of your email: 1. You're using no-clean paste. 2. This is only happening on the second side. You tell me if I'm wrong about this... First thing, if you're only experienc
Electronics Forum | Wed Oct 10 20:54:32 EDT 2001 | davef
We're with the Ozzy's earlier posting on this thread. We make similar products, like: * Phantom products that are mostly complete and then are configured to order by adding or subtracting a couple of parts and some jumpers. * Version products like y
Electronics Forum | Wed Sep 01 08:27:38 EDT 2004 | davef
Zinc from the brass [Cu3Zn2] diffuses into the tin causing solderability problems. Just 0.001% of Zn in your solder can render it fit for the scrap heap. So, you need a barrier plate between the brass and the tin. Copper or nickel-plating is commonl