Electronics Forum | Mon Jul 24 11:35:42 EDT 2006 | Jimk@ics-inc.org
We have experienced a problem with tin leaching or discoloration of lead terminals on random parts on solder side of a paste/paste operation. The profile has been used on previous production runs and there doesn't appear to be any heat damage to othe
Electronics Forum | Thu Jul 27 07:50:35 EDT 2006 | davef
Send us pix
Electronics Forum | Wed Aug 17 13:57:27 EDT 2005 | ppwlee
We have encountered what appears to be mask discoloration after wave soldering. The areas of concern coincide with the areas that were exposed selectively by fixtures during wave soldering, dominated by one date code of PCB with a slightly different
Electronics Forum | Wed Aug 17 22:41:37 EDT 2005 | davef
Peter are you having fun with solder masks erwat? We saw this years ago with LPI solder masks. It shows occasionally with other masks. We agree with Russ. If nothing [eg, alcohol, flux thinner, acetonitrile, or water] dissolves the haze, then it
Electronics Forum | Wed Aug 17 14:30:58 EDT 2005 | russ
I usually see this with mask that is not fully cured from the PCB shop. This probably agrees with the baking statement that you made.
Electronics Forum | Sun Feb 12 22:52:20 EST 2017 | ltchsze
Hi fellow professionals, Wondering whether anyone has experience with solder splashing from component terminal. Have identified the source using the component without printing solder paste on PCB. Wondering the root-cause of the solder splashing fr
Electronics Forum | Mon Feb 13 10:41:14 EST 2017 | dyoungquist
Could be that your temperature ramp up rate is too fast. This could cause the flux in the solder paste to burn off too rapidly. When that happens, it can expand as it heats up and burns off, causing the solder to get spread out from the pad.
Electronics Forum | Thu Jan 20 11:20:28 EST 2000 | Brian W.
It sounds like what you are seeing is leaching of the end cap. You need to check the manufacturer's spec. Many components have terminal barriers, which get a solder plating. Sometimes this plating process is not done well, and the solder plating le
Electronics Forum | Tue Feb 21 16:39:03 EST 2017 | ltchsze
Thanks for input, dyoungquist. The condition here is without any flux or paste applied. Solder from component terminal started splashing by itself when put through re-flow.
Electronics Forum | Thu Jan 20 11:16:51 EST 2000 | Wolfgang Busko
Erico:I can�t even imagine what this line looks like and what it has to do with the soldering problems without having a look at it. Also the restriction to touchup only is somewhat irritating to me. The only thing that I can think of is that in your
.gif)