Electronics Forum | Fri May 14 16:24:35 EDT 1999 | Chrys Shea
| | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | Thanks | | Wes Ruggl
Electronics Forum | Sun Apr 25 14:43:34 EDT 1999 | Earl Moon
| | Hello all, | | | | Our guys here still have some questions on the "optimized" profile which sees a more moderate ramp up straight to reflow temperatures versus the conventional profile which has a plateau at around 150 Celsius. If the optimized
Electronics Forum | Sun Apr 25 11:50:08 EDT 1999 | Earl Moon
| | | We are just starting to manufacture a PCB with a .039" fine-line PBGA. We are currently seeing voids, mainly in the center, that are as much as 45%. We also intermittently see the corner balls of the PBGA smaller than the center balls. We are u
Electronics Forum | Tue Apr 20 17:56:42 EDT 1999 | Chrys Shea
| | I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following
Electronics Forum | Tue Apr 20 22:09:03 EDT 1999 | Earl Moon
| | I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following
Electronics Forum | Mon Mar 15 09:38:30 EST 1999 | Chrys
| Does anyone have any recommendations on spray fluxers? Are there major differences between the high priced ultrasonic machines to the low priced flux/air spraying machines? We are going to be spraying an OA flux with 11% solids content. Are there a
Electronics Forum | Mon Mar 15 15:42:16 EST 1999 | George Steele
| | Does anyone have any recommendations on spray fluxers? Are there major differences between the high priced ultrasonic machines to the low priced flux/air spraying machines? We are going to be spraying an OA flux with 11% solids content. Are there
Electronics Forum | Mon Mar 08 20:17:41 EST 1999 | Michael Larsen
| | I'm having a fun time between BGA rework/repair using an SRT 1000 and SPC efforts (much easier) using DEK stencil printing processes and BTU reflow with 6 Fuji lines in between. | | Concerning the BGA stuff, I'm getting about 60% success using
Electronics Forum | Tue Feb 16 16:25:18 EST 1999 | Tuffty
| We use both F4G and MCS at the present and we are phasing out MCS. One main reason is that it's platform is not Y2K compliant. F4G is cumbersome and taxes a high overhead on your computer system. We have also found a bug recently when we have hi
Electronics Forum | Sun Jan 31 03:28:24 EST 1999 | Jeff Sanchez
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde