Electronics Forum: double and reflow and off (Page 1 of 8)

01005 components and reflow profiles

Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101

I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the

Re: Pb alloy reflow temperatures and component integrity

Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee

If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC

Time and temp in lead and lead-free reflow

Electronics Forum | Mon Jul 28 16:48:54 EDT 2008 | pcbbuilders

my oven has a built in profiler, it works fairly well, but it can not predict changes. my main concern was about the time right before reflow. i know that's where the flux is activated and i was worried that i may be spending too much time at the tem

Time and temp in lead and lead-free reflow

Electronics Forum | Sat Jul 26 07:42:49 EDT 2008 | pcbbuilders

I am not very concerned about production time, but it is always a thought! Quality is more importnant of course. We have 2 different pastes, with almost identical requirements. We can get close to their profiles, but i am worried that i am spending

SMT solder reflow clamps, pushers and pullers for tooling

Electronics Forum | Mon Apr 16 18:49:40 EDT 2012 | tris101

Hi guys, I'm looking for some tooling parts and I hope you can point me in the right direction. We design basic in house reflow Carriers to surport boards during reflow. I would like to add clamps to our designs but I can not locate any off the she

Cracking Capacitors and Solder Balls

Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan

Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have

small and good pick and place machine

Electronics Forum | Thu Sep 05 23:18:03 EDT 2013 | feiyangniao

There is a new toy I received today: a NeoDen TM-240A automatic desktop pick and place machine! I’ve kept my eyes on this baby for a quite a while, and finally decided to make a purchase last week. The shipping was very fast: DHL from China, a total

Immersion gold and BGAs

Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David

Where could I find more information regarding the double sided reflow and flux problems with white tin?

0402's and Gluing.............

Electronics Forum | Wed Feb 09 18:22:20 EST 2005 | mrduckmann2000

Valerie, Thank you for your reply. I have a quick question......when you converted to a double reflow process did you have any thru-hole parts on the assembly. If so how did you handle them....pin and paste? Thanks, mike

Immersion gold and BGAs

Electronics Forum | Wed Aug 31 12:33:25 EDT 2005 | Jaya

I have expirence running,double sided Imm gold boards recently which ed up a lot of solderability issue. The Imm gold need to be slightly more control during reflow oven area on it's profile.

  1 2 3 4 5 6 7 8 Next

double and reflow and off searches for Companies, Equipment, Machines, Suppliers & Information

Best SMT Reflow Oven

World's Best Reflow Oven Customizable for Unique Applications
Void free Reflow Soldering

ONLINE IPC Training & Certification
SMT feeders

Repair tools for all your electronic circuit board repair needs.
IPC Training & Certification - Blackfox

Easily dispense fine pitch components with ±25µm positioning accuracy.