Electronics Forum | Mon Apr 17 19:30:27 EDT 2000 | Boca
All of the above is good stuff. To add, I have seen this several times if the assembly is wavesoldered. Heat from the wave can partially reflow the top side SM solder joints and weaken them. To test, check joint strength before wave and then after
Electronics Forum | Tue Apr 11 16:42:56 EDT 2000 | Chad Notebaert
I�m thinking �Poor intermatallic� It could be a few things. Lets start at the beginning. -Is your paste a 63/37 mixture? -Have you monitored you screen printing, Verify Solder deposition, Are you getting enough paste? -You say the solder looks like i
Electronics Forum | Mon Sep 22 17:02:58 EDT 2008 | hegemon
You are on the right track Ismir. Essentially however, as the programmer of the machine, I am the one that creates the PCB with the errors to benchmark the settings for the machine. No secret lab though! :-) Easy enough for most any AOI machine to
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Thu Sep 05 23:18:03 EDT 2013 | feiyangniao
There is a new toy I received today: a NeoDen TM-240A automatic desktop pick and place machine! I’ve kept my eyes on this baby for a quite a while, and finally decided to make a purchase last week. The shipping was very fast: DHL from China, a total
Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Wed Feb 09 18:22:20 EST 2005 | mrduckmann2000
Valerie, Thank you for your reply. I have a quick question......when you converted to a double reflow process did you have any thru-hole parts on the assembly. If so how did you handle them....pin and paste? Thanks, mike
Electronics Forum | Wed Aug 31 12:33:25 EDT 2005 | Jaya
I have expirence running,double sided Imm gold boards recently which ed up a lot of solderability issue. The Imm gold need to be slightly more control during reflow oven area on it's profile.
Electronics Forum | Fri Oct 30 10:17:05 EDT 2015 | esoderberg
You don't say how many headers you have to solder. I usually spec in High temp headers and use a pin-in-paste methodology and double reflow. Can you get your headers high temperature?
Electronics Forum | Sat Feb 17 14:21:54 EST 2007 | Muhammad Haris
Hi All, I am using YV100Xg YAMAHA Pick and Place Mounter Machine and I am facing a tilting problem of PLCC 84 and QFP 240 pins ICs. I deeply checked about their vision files and place them on the double sided tape and found them ACCURATE on their pad