Electronics Forum | Wed Mar 31 20:49:11 EST 2004 | marcowong
We are trying to buy used double wave solder and ICT machine and we need some advice on selecting the machine and things to be cautious with. It will be greatly appreciated if someone can offer us good suggestions that will help us to minimise mist
Electronics Forum | Wed Mar 31 21:27:00 EST 2004 | marcowong
Dear Darren, Please provide more information of your machine, selling price and where it is at the moment. If it is not in Penang malaysia, please also let us know the transportation cost too. Thank you.
Electronics Forum | Thu Apr 01 08:44:58 EST 2004 | pjc
Be smart, be skeptical and be educated on the machines you are looking at. If you are going to do business with someone you don�t know, check them out. Ask others in your region and get at least ten customer references from them.
Electronics Forum | Wed Mar 31 21:02:53 EST 2004 | darburch
If you find your self interested in an electrovert machine we have a UP600 for sale, a good machine if you have experience with electrovert. As for a buying guide I'm not sure if there is a reliable source who has compared the different models.
Electronics Forum | Fri Apr 02 02:37:43 EST 2004 | darburch
We are asking $10,500us for this machine, as for shipping I will see what I can come up with as we are in Canada. This is a dual wave machine with foam fluxer. It has not run in 3 years but when we had it in production results were favorable and cons
Electronics Forum | Mon Mar 22 09:37:28 EST 2004 | ellis
After 2nd time reflow of double reflow, wrinkles solder joints found on SOIC and SOT components.(only happen on the components at the underside of pcb during reflow, top side components dont have this problem) is this due to the reflow process proble
Electronics Forum | Mon Mar 22 10:24:03 EST 2004 | davef
Wrinkled like orange peel?
Electronics Forum | Mon Mar 22 19:46:17 EST 2004 | pdeuel
The bottom side is going into reflow somewhare near melting point of solder. Reduce bottom side temprature. Get a good mole so ramp and soak tempratures can be checked on bolth sides of the PCB. The object is to keep bottom side parts from approching
Electronics Forum | Wed Mar 24 08:36:58 EST 2004 | Evtimov
Hi! What exatly you do? Do you reflow the both sides of the board at the same time or you reflow your second side? I think in both cases you should decrease you bottom zones. If you reflow both sides - with 10-20C(F) If you reflow the second side - w
Electronics Forum | Tue Feb 09 11:23:25 EST 1999 | michele sommaruga
I would like to have information about the processability of different packages. In particular I would like to known for which package I can use a double reflow for soldering. Best Regards