Electronics Forum | Wed Nov 06 05:13:01 EST 2002 | Dreamsniper
Crystalline flux if it is really clear should not be a problem. We were using Amtech paste before and we have the same results. Sometimes we mistakenly see it as a dry joint because of the reflections from the lighting of our Metcal inspection system
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Tue Apr 10 04:16:20 EDT 2012 | grahamcooper22
you are seeing a typical issue that is caused when such small volumes of paste are printed....there are several reasons for it..the tiny amount of flux in the small deposit becomes exhausted much quicker then it does in a larger deposit ( the flux ma
Electronics Forum | Fri Jan 28 12:18:32 EST 2005 | Chunks
Your best bet is to do a decision making matrix. Each company has so many different criteria�s it's hard to pick out which one might be important to yours. Simply pick out your top 5 paste manufactures. Next decide what your "Eliminators" are - th
Electronics Forum | Mon Nov 02 14:45:25 EST 2015 | stevezeva
Hi there! If they are just standard headers there's a company called Teka that makes headers and socket headers with solder preforms in them. They call it "Solder Bearing Lead Technology" You can drop them in the board and reflow them just like SMT p
Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Mon Apr 18 10:07:19 EDT 2011 | wrongway
Hello Jebs we started out that way but the more handaling of the pcb the more problems you will have if you can do it in line and have the pcb's stop at some of the conveyors you can do some inspection. yes all of our machine's are in line now we lo
Electronics Forum | Mon Mar 13 14:26:45 EST 2006 | Wave Master Larry
Well, im not sure what plane you guys are on, but I can back up my what im talking about. Ya see I wnet to Soltec traingin back in 1995 for our new wave. I got a diploma proofing that I know what i'm talking about. no one else in my company has on