Electronics Forum | Tue May 23 21:14:22 EDT 2006 | davef
First, where the temperatures that aare mentioned in the original post measured? Second, it sounds like the PdAg component terminations are not seeing enough heat [your soldering iron touch-up proves this]. Your 232*C peak is the absolute minimum s
Electronics Forum | Wed May 14 12:35:34 EDT 2008 | rgduval
Thanks, Chunks. That's the one point of the experiment that we haven't tried yet. Though, we came to the same conclusion just yesterday. Dave, so far, the most help we've gotten was from the paste manufacturer. I've involved the board house, but
Electronics Forum | Tue Jul 27 17:23:45 EDT 1999 | M.L
| | | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | | 12BGA per assembly | | | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | | Pads .014inch | | | | Vias within footprint .020inch | | | | Vias to be filled by b
Electronics Forum | Tue Apr 20 22:09:03 EDT 1999 | Earl Moon
| | I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following
Electronics Forum | Thu Apr 15 10:05:50 EDT 2010 | dwonch
Hi all, Long story ahead.... We are having issues with board vendors on some of our higher layer count (thick) boards. Specifically under BGAs with high aspect ratio vias (14:1). We are using ENIG finish and a lead free process. Basically we get t
Electronics Forum | Fri Jun 27 10:27:59 EDT 2003 | davef
Since you�re asking the question about proper handling of OSP board, there may still be time to talk you out of using that material. * Cleaning of mis-printed board could cause non-wetting problems. This tends to remove a fraction of OSP coating. 0.3
Electronics Forum | Tue Jul 27 16:44:31 EDT 1999 | Earl Moon
| | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | 12BGA per assembly | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | Pads .014inch | | | Vias within footprint .020inch | | | Vias to be filled by bottom side(sol
Electronics Forum | Mon Jun 28 22:02:13 EDT 1999 | Dave F
| Hey there gang, how's it going ? | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's ar
Electronics Forum | Tue Apr 20 17:56:42 EDT 1999 | Chrys Shea
| | I am wondering if anyone has any info regarding solder paste misprint clean-up procedures for Entek Plus CU-106A PCB's utilizing a water-clean solder paste. In a implementation procedure they recommend a 2-3 minute wash cycle with the following
Electronics Forum | Mon Jan 19 20:01:11 EST 1998 | Steve Gregory
| We use no clean paste and sometimes experience | flux splattering which gives spot on gold fingers. | Need help in analize the cause. thx. Dominic, That is STILL a problem huh? It's a tough one to solve sometimes...especially when you have as