Electronics Forum | Fri Aug 25 08:12:16 EDT 2006 | davef
Leading conveyor manufacturers are ATI, Conveyor Technology, Crown Simplimatic, Dynapace, Flextek, Fuji, Jot, Kanetic, Panasonic, and Process Control.
Electronics Forum | Sat Apr 14 10:21:30 EDT 2007 | HOSS
We are processing a 5x22" PCB using Juki "2010E and 2060E". Machines are spec'd as 18x20" cabable. We just needed to adjust a conveyor sensor (1 time) and ignore a few placement area warnings.
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Mon Apr 09 10:16:14 EDT 2007 | davef
Pick and place: * Fuji: The largest pcb size is 20" by 18" for pick and place; 18"x14" for chip shooters. Fuji NP XL series allows 27 by 23 inch boards using a conveyor. * MYDATA has machines that can be configured to 34" X 44" X 0.500" * HSP 4796A a
Electronics Forum | Fri May 15 21:39:48 EDT 2015 | jlawson
Reflow.. 1.Rehm (Germany) - Best in Class Best overall process stability heating system ( Alot of makers have started to copy there VX heating arrangement ). COnveyor chains can be a bit more attention in terms of maintenance on rehm , but if foll
Electronics Forum | Fri Nov 30 00:51:10 EST 2007 | vinitverma
Here are the differences (Eclipse vs Eclipse II) Optimum Speed: 5000 vs 6500cph Feeder Positions (8mm) : 80 vs 94 PCB Loading Time : 4s vs 5.3s PCB Thickness : 0.6-3mm vs 0.5-4mm Max Component Size : 32mm vs 45mm (optional camera possible on Eclipse
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Tue Oct 27 15:25:02 EST 1998 | Stefan W.
Hi Samson ! In order to give you more detailed information I would like to know what your component range is and how many boards you supposed to do. Panasonic and MPM are a good choice, however, Panasonic has not many P&P machines on the U.S. market,
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT