Electronics Forum | Tue Sep 18 15:35:23 EDT 2001 | jschake
A laser cut stainless steel stencil was used exclusively for the evaluation of the complete 0201 assembly process, which addressed printing, placement, and reflow. However, I have also conducted off-line 0201 print tests using a nickel electroformed
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Thu May 02 07:11:10 EDT 2002 | davef
They probably the same. Most likely someone is saying immersion gold [immersion Au] as a short hand for ENIG [ Electroless Nickel - Immersion Gold]. It is very uncommon to plate gold directly on copper, because gold and copper form a brittle interm
Electronics Forum | Thu Oct 21 14:02:32 EDT 1999 | Ron Costa
We are a contract manufacturer currently building a job with IBM CBGA-255 devices and 20mil QFP's that are close to each other. We use a 6 mil laser cut and electro polished stencil with one to one apertures on the BGA's. The customer is experiencing
Electronics Forum | Thu Jan 12 02:08:47 EST 2006 | adeline_ko
Hi, What is the different between Electroless Nickel / Immersion Gold (ENIG) and Immersion Au. Are they refer to the same finishing? We has been using the Gold thickness (0.00005 - 0.00013mm) , nicket (0.0025mm) for all Gold finishing brd (Immersio
Electronics Forum | Thu Jan 12 10:05:13 EST 2006 | davef
There's a lots comparisons like this on the web. Here's one: Westwood Associates said on 8/12/2003: ||HASL||OSP||ENIG||Pd||Tin||Silver Flat||no||yes||yes||yes||yes||yes Solderjoint||Cu-Sn||Cu-Sn||Ni-Sn||Ni-Sn||Cu-Sn||Cu-Sn Contact||E-test, ICT||no|