Electronics Forum | Sat Feb 18 13:23:49 EST 2006 | CW
thanks for the reply GS. Do you know what does those condition mean? what is saturated 30C/85% RH???? i need to understand this before i could release my procedure and provide training to the operators
Electronics Forum | Thu Apr 20 14:08:34 EDT 2006 | cw
hi All, recently i have received some parts with the lead turning black, and i then found out the leads are silver plating, is that going to be a problem? or it is simply a cosmetic issue? pls advise ASAP!! thansk a lot!!
Electronics Forum | Wed Feb 15 19:34:05 EST 2006 | Sang Jun Kim
Ran across this at APEX Show in California, seems like it has good potintial for supporting PCB Boards good. We are assigned project to find solution to support PCB. Anybody have exerpeince with this?
Electronics Forum | Thu Feb 16 03:43:54 EST 2006 | aj
hi, we tried to introduce form-flex a few years back and it caused more problems than it fixed. Switched back to pins and no problems. It might have improved since but I would be reluctant to get them again unless I was given a 6 month trial!! aj
Electronics Forum | Wed Feb 15 21:49:40 EST 2006 | Jose Luis Mendoza
Hi there,, Im looking for information about history and evolution of the PIH process. I will use this information for the state-of-the -art in my Master.D tesis project. Any information will be appreciate! Regards. Jos� Luis Mendoza ITESM
Electronics Forum | Fri Feb 17 19:36:09 EST 2006 | mika
You can also take a look at http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=9902&mc=2 /Mika
Electronics Forum | Wed Feb 15 21:54:07 EST 2006 | Jose Luis Mendoza
Hi there,, Im looking for information about history and evolution of the PIH process. I will use this information for the state-of-the -art in my Master.D tesis project. Any information will be appreciate! Regards. Jos� Luis Mendoza ITESM jlmen
Electronics Forum | Fri Feb 17 14:55:36 EST 2006 | Mity-C
Jobbie, We are also not using the Mydata forks for the vibe feeders. We take a tube for the vibe component and cut a pick pocket. We use the back of the forks as stops. This has eliminated many of the pick problems from the vibes. Good Luck Chris
Electronics Forum | Thu Feb 16 11:42:29 EST 2006 | russ
I use Alpha 857 W.S. for wave is that what you mean? If so, I love this stuff, it solders everything. one downside to it is convection (wave , rework) can dry it out and leave white hazes and even residues at the joints.
Electronics Forum | Mon Mar 13 11:22:56 EST 2006 | James Lalicker
I have been using Alpha 856 for about 8 years. It is an excellent flux. Today we are using it in a new flow solder machine that has a spray fluxer and it seems to be working fine. I can be contacted at jlalicker@amitulsa.com