we are encountering a problem on our production. after dipping a copper wire AWG#30 to a leadfree solder the wire becom thinner and easily to break. does the leadfree soler has the capability to weaken the wire (lessen the diameter)after dipping to l
Electronics Forum | Wed Nov 02 22:06:54 EST 2005 | davef
Slaine, our intuition is the same as yours [that 100Sn should dissolve the copper faster than other solders]. Bob Gilbert's FCT data shows otherwise. Look here: http://www.fctassembly.com/newsltr/2004/0804/Aug04.htm
Electronics Forum | Wed Nov 02 14:45:26 EST 2005 | chunks
Here's the info on Gel Flex: http://www.adhesivesmag.com/CDA/ArticleInformation/products/BNPProductItem/0,2109,120109,00.html http://www.speedlinetech.com/docs/Gel-FlexBrochure.pdf#search='Gel%20flex' I agree, the Grid Loc was not all it was crake
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Thu Nov 03 09:43:55 EST 2005 | lupo
Check flux penetration and type of flux. How much is solid contents. The solder filling is better under Nitrogen. Check the time (speed) of the nozzle whether is correct. Usually For SAC305 the temperature of bath is 320C/degrees, but only for sel
Electronics Forum | Wed Nov 02 12:41:07 EST 2005 | Tapesplice.com
Tape Splicer and Tape Splicing Products for splicing a seamless reel of SMD Components. Tape Splicing increases throughputs and yields by 15-20%. We also manufacture Antistatic Clean Room Lab Coats, Clean Room Coveralls, ESD Grounding Straps, Cleanro
Electronics Forum | Wed Nov 02 16:09:50 EST 2005 | jrr3434
My company is looking into buying a batch reflow oven to run quanties varing from 10 to 50 boards per week. Can any one tell me what are the limiations of these ovens? How well can they actually do lead free? What kind of through put can I expect?
Electronics Forum | Thu Nov 03 04:17:07 EST 2005 | Slaine
we had the same problem of getting rid of the heat from the oven. we set up an air line to blow into the oven after parts had been removed that helped a bit. I dont like using them because the profile is not the same every time.So where possible i p
Electronics Forum | Thu Nov 03 11:23:40 EST 2005 | JeffP
Jay, What are your board sizes? What is the maximum size that you envision reflowing? 10-50 boards a week . . . is that in a single run or broken down into a few boards a day/hour? Do you have a high mix or is it a single product? Are the boards