Electronics Forum | Wed Mar 16 20:11:03 EST 2005 | darby
KT, What sort of delta T are you getting? This does sound a bit odd. TCs are in EXACTLY the same position on each board? Something I only recently found out - according to Mark Cannon from ERSA re profiling, that you may wish to consider. 1.TCs sho
Electronics Forum | Thu Mar 24 07:06:06 EST 2005 | davef
There's a lot of comparison tables on the web. Here's one: Properties - Summary [A Winlow Circatex] Attribute||Hasl||Immersion Silver||Immersion Tin||Electroless Pd||OSP||Eless Ni / Imm Au Shelf Life (months)||12||12||12||12||12||6 Multiple Reflows
Electronics Forum | Thu Mar 17 10:56:24 EST 2005 | jmedernach
Hi John, This problem is interesting. I've never had a problem with solder shorts caused by subjecting a device to reflow a second time. I've built many double sided SMT assemblies with fine pitch devices on top and bottom. Some things to possibly
Electronics Forum | Fri Mar 18 14:21:02 EST 2005 | Dreamsniper
We are producing control products for the Aerospace Industry both Commercial and Military. I have TQFP 100 fine Pitch in one of my PWB's Solder Side and have no misalignment problems or defects on my part after 2nd reflow. I control my reflow profile
Electronics Forum | Fri Mar 18 19:17:37 EST 2005 | valuems
Hello PMD Don't feel like that, we live with these MPM's. And we have over 10 years experience. Also never mess with the down stop on any MPM and you will be better off. Most of mpm's machines have a down stop of .0750 and it should never be cha
Electronics Forum | Fri Mar 18 07:51:00 EST 2005 | jh0n
I'm currently trying to do a complete backup of a GSM-1. It's older, and only has one IDE connector (can't add another HDD), and no CD-R. We're having trouble with TCP/IP too. Given that floppy is my only way out right now, and that's pretty unatt
Electronics Forum | Mon Mar 21 02:51:23 EST 2005 | amstech
I have done few thermocouples using high lead solder, silver epoxy that is used for die attach purposes and some X - non conductive material. Though all materials show a slight variation in temperatures (3 to 5 degree C), the dwell time at peak is qu
Electronics Forum | Mon Mar 21 07:25:12 EST 2005 | cyber_wolf
We have lab sink in our SMT area that we use for washing off stencils and hand tools that are contaminated with solder paste. The sink has a float in it and when the water level reaches a certain point it pumps the main basin out through a filter th
Electronics Forum | Tue Mar 22 06:08:45 EST 2005 | Grant
Hi, We used to manually profile by comparing logged temp numbers and matching the paste profile. But we got a KIC and it's software was so much better we got a good reduction in rework and we have almost no first run faults now. I would recommend on
Electronics Forum | Tue Mar 22 07:39:05 EST 2005 | davef
There is no standard. This is a relative test. If you wish to do tests of this kind, we suggest to pay attention to the following points: * Shear strength of soft solder depends on the deformation speed applied. The faster the material is deformed t