Electronics Forum | Tue Jan 04 12:37:41 EST 2005 | Cmiller
We have been using this finish almost exclusively for fine pitch boards for about 5 years. Make SURE you use a board house that does the gold plating in-house. There are some potential issues as DaveF stated. The only problem we have encountered is w
Electronics Forum | Tue Apr 11 10:30:46 EDT 2000 | Jeremy Smith
I am having a problem with some joints on a 100 pin pqfp and few different soics on one particular board. When viewed a 8x with a "Mantis" inspection scope the joints look as though they wetted to the ic leg but when probed the leg will pop loose.
Electronics Forum | Tue Jan 15 06:05:37 EST 2002 | Romain
Dear all We have since few weeks problems with BGA solder joint integrity on ENIG finish. Under relatively very flexible of the FR4, the joint breaks between ball and PWB. When we take off the BGA for analysis, some of the pads seem very flat, totaly
Electronics Forum | Mon Apr 17 19:30:27 EDT 2000 | Boca
All of the above is good stuff. To add, I have seen this several times if the assembly is wavesoldered. Heat from the wave can partially reflow the top side SM solder joints and weaken them. To test, check joint strength before wave and then after
Electronics Forum | Fri Jun 08 17:22:51 EDT 2007 | naynayno
We have been producing an IMS assembly with SMT dpak's for some time. However, we recently encountered a new problem by chance - the parts can be flicked off with a finger nail. I state by chance because the solder joints are wetted and shiny with
Electronics Forum | Tue Apr 11 14:59:05 EDT 2000 | Glenn Robertson
Jeremy - What's the process flow on these modules? Are they wave soldered? What is the board finish (ENG, HASL, etc.)? Glenn Robertson
Electronics Forum | Tue Apr 11 20:26:16 EDT 2000 | Dave F
Jeremy: Parts assembler make leads of either Alloy 42 (Invar, whatever) or copper. The solderability of these leads are protected with eutectic or non-eutectic tin/lead solder, palladium or some palladium alloy, or gold. Cuppla things to consider:
Electronics Forum | Tue Apr 11 16:42:56 EDT 2000 | Chad Notebaert
I�m thinking �Poor intermatallic� It could be a few things. Lets start at the beginning. -Is your paste a 63/37 mixture? -Have you monitored you screen printing, Verify Solder deposition, Are you getting enough paste? -You say the solder looks like i
Electronics Forum | Fri Jun 08 18:27:03 EDT 2007 | jmelson
This is probably an inner plated layer of the component that did not bond well. It may be a component that either has the wrong surface finish for lead-free or can't handle the temperatures. Many times I have seen a similar-looking layer when the l
Electronics Forum | Thu Jan 08 15:49:10 EST 2015 | emeto
I bet you that the problem comes from the ENIG brittle solder joints. About low temperatures I think you can go to the absolute 0 and the device should still work.