Electronics Forum | Sun Apr 25 17:30:25 EDT 1999 | Mohammad Yunus
| | | | We are just starting to manufacture a PCB with a .039" fine-line PBGA. We are currently seeing voids, mainly in the center, that are as much as 45%. We also intermittently see the corner balls of the PBGA smaller than the center balls. We are
Electronics Forum | Fri Jul 24 02:32:35 EDT 1998 | Frank J. de Klein
| Hi, | We have encountered one serious problem that heavy packages falling down during second side reflow, especially for PLCC 84. I believe it caused by temperature profile setting. | Any good suggestion would be highly appreciated! | Stoney Tsai *
Electronics Forum | Fri Jul 24 10:36:48 EDT 1998 | Dave F
| | Hi, | | We have encountered one serious problem that heavy packages falling down during second side reflow, especially for PLCC 84. I believe it caused by temperature profile setting. | | Any good suggestion would be highly appreciated! | | Stone
Electronics Forum | Fri Jul 10 14:16:06 EDT 1998 | Bob Willis
As Steve said there should not be a problem with cracking plastic components but if you are reaching 180c there will be a problem with secondary reflow on the top side of the board. PCBs flex during wave soldering as they do during reflow if not supp
Electronics Forum | Thu Jun 25 10:32:51 EDT 1998 | Gary Simbulan
Alright gentlemen and ladies of the forum, I again seek knowlage on what is probably a well known fact. I have spent a good part of the morning with various IPC standards and weighty tomes such as the Electronic Packaging and Interconnection Handboo
Electronics Forum | Thu Jun 25 14:41:07 EDT 1998 | Earl Moon
| Alright gentlemen and ladies of the forum, I again seek knowlage on what is probably a well known fact. I have spent a good part of the morning with various IPC standards and weighty tomes such as the Electronic Packaging and Interconnection Handb
Electronics Forum | Thu May 28 08:56:12 EDT 1998 | Earl Moon
| I have a component that is glue cured on the bottom of a pcb. The component is a 1206 size jumper. It is made up of iron/nickel alloy. The problem I am having is that the part will fall off the board during wave solder. Is the component not abl
Electronics Forum | Wed Mar 11 10:58:58 EST 1998 | Earl Moon
| | What does the term "poor wetting" mean as a defect code ? "Poor" should mean unacceptable when surface (component or PCB solder termination areas) wetting does not provide acceptable solder joints. Unacceptable wetting of PCB solder termination
Electronics Forum | Wed Dec 31 23:02:19 EST 1997 | Scott McKee
| Has anyone had any experience with thermal shocking | and cracking of SMD capacitors during the rework process? | My company was advised to preheat capacitors to 125 C | at a rate of 2 C/sec before replacing them onto boards. | Would this maybe
Electronics Forum | Mon Dec 29 14:42:00 EST 1997 | justin medernach
| Hello all, | I have experienced broken ceramic SMT parts. Most of the time, | we have found fractured inductive beads. Once in awhile, we find | broken Ceramic Caps. All parts we use are 1206 form factors and | we use tape and reel... | Michael
.gif)