Electronics Forum | Mon Jun 14 08:48:29 EDT 1999 | Adam Pratt
| | | Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down from man
Electronics Forum | Mon Jun 14 11:39:29 EDT 1999 | Marshall
| | | | Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down from m
Electronics Forum | Thu Jun 17 10:37:42 EDT 1999 | Brian Wycoff
| | | | | Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down from
Electronics Forum | Thu Jun 17 11:18:03 EDT 1999 | Ian Clelland
| | | | | | Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down fr
Electronics Forum | Sat Mar 06 12:33:21 EST 1999 | Dean
| | I'm having a fun time between BGA rework/repair using an SRT 1000 and SPC efforts (much easier) using DEK stencil printing processes and BTU reflow with 6 Fuji lines in between. | | Concerning the BGA stuff, I'm getting about 60% success using
Electronics Forum | Mon Mar 08 05:11:36 EST 1999 | Earl Moon
| | | And on it goes. Again, I can't thank you enough for your time. I will call you soon as others probably find this rhetoric a bit much. | | | | Earl Moon | | | Earl and Dean, | | No,no,no...please continue here. I've been gratefully rea
Electronics Forum | Tue Sep 15 12:11:36 EDT 1998 | Bill Schreiber
Jeff, The use of flux thinner would only add another chemical to the process. Environmentally, that would not be a good idea. My guess is that you would only end up with "thinner jelly" anyway. Alcohol works well on RMA flux. When assemblers switch f
Electronics Forum | Wed Apr 15 15:04:18 EDT 1998 | D. Lange
| | | | We are having a bridging problem with SOIC 14,16 and 20 pin devices during flow solder of the bottom side of our boards. This bridging occurs about half way up the lead between the board and the body of the IC. The chip parts are no proble
Electronics Forum | Wed Apr 15 14:57:20 EDT 1998 | D. Lange
| | | | We are having a bridging problem with SOIC 14,16 and 20 pin devices during flow solder of the bottom side of our boards. This bridging occurs about half way up the lead between the board and the body of the IC. The chip parts are no proble
Electronics Forum | Wed Apr 15 14:53:06 EDT 1998 | D. Lange
| | | | We are having a bridging problem with SOIC 14,16 and 20 pin devices during flow solder of the bottom side of our boards. This bridging occurs about half way up the lead between the board and the body of the IC. The chip parts are no proble