Electronics Forum | Thu Jul 29 23:21:51 EDT 1999 | CH Lee
I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. This ceramic substrate
Electronics Forum | Thu Sep 12 11:50:58 EDT 2002 | stepheno
http://www.jedec.org/download/search/jstd020b.pdf http://www.jedec.org/download/search/jstd033a.pdf The above links are for JEDEC standards regarding moisture sensitivity. SMT magazine has an article a few months ago regarding a company that saved
Electronics Forum | Wed Oct 19 07:44:33 EDT 2005 | davef
When a hole is drilled during board fabrication, it can transfer resin from the base material (eg, FR4 core or prepreg) to cover the exposed edge of conductive material in the wall of a drilled hole. This is called resin smear. Etchback is a control
Electronics Forum | Wed Oct 26 20:20:28 EDT 2011 | machinehead
Our Company is suffering a Huge lose in scrap parts. I recently took over the My12 MyData SMT Machine. And I'm trying to find a remedy to the lose of exposed parts when pulling tape out of feeders. I've tryed alot of things? But still no Luck. I'm lo
Electronics Forum | Wed Dec 09 10:45:56 EST 2015 | huske
I've put down a SOT223, close enough to your 3pin transistor, in the same situation you have. The large pin was to be soldered on a large exposed ground plane in the corner of a board, over 2"x2" exposed area. We left the paste file as is, so where
Electronics Forum | Fri Jul 09 11:39:27 EDT 2021 | stephendo
I was once part of a conference call with a component manufacturer. The call was starting to get heated as the manufacturer was certain that we were not storing the parts properly and we knew that we were. Then one of their people asked how many we
Electronics Forum | Thu Jun 01 10:48:21 EDT 2000 | Jeremy
I am having a problem with the green solder mask flaking off exposing bare copper. The mask was defective from the board manufacturer. My problem is the boards are already assembled and we are just finding the problem. Is there a standard that cover
Electronics Forum | Wed May 24 11:21:32 EDT 2000 | Travis Slaughter
Its my understanding that so long as the paste is not exposed to air it is not going to be active, someone else might be more sure about this than I am. Be ready for lots of half soldered leads using this process. Its quick and easy but will not b
Electronics Forum | Sat Apr 14 03:25:04 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that
Electronics Forum | Sat Apr 14 03:25:10 EDT 2001 | kpliew
Hi , As far as I experienced with wave reflow. If u have a refective thermal reader , u will see that the board is exposed to much more temp than the 120 deg that u set. Actually , once u see the board warp or comp. crack u should know that