Electronics Forum | Fri Oct 20 14:13:32 EDT 2000 | DENNIS XIONG
Dear all, We have a PCB design mistake that causes exposed copper layers on the edges of breakaway locations. Although we fixed the design, but we already made a lot of boards plus many made before we found the problem. I wonder if any one have some
Electronics Forum | Sat Oct 21 03:55:14 EDT 2000 | DL
Dennis, I've seen this before, and in our case we didn't need to seal the edges because there was no concern of shorting or anything in the end product, this is a choice you will have to make, Does your end product have any protrusions or mounting h
Electronics Forum | Thu Jan 14 09:25:34 EST 2016 | davef
IPC-A-610F 10.2.6 Laminate Conditions - Depanelization talks to the acceptability of the depanelization criteria for assembled boards. There is no requirement for moisture sealing with epoxy or other material. Basically, the standard requires that th
Electronics Forum | Thu Jul 29 23:21:51 EDT 1999 | CH Lee
I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. This ceramic substrate
Electronics Forum | Fri Jul 30 14:50:26 EDT 1999 | Kevin Hussey
| I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | This ceramic substr
Electronics Forum | Fri Jul 30 16:02:49 EDT 1999 | Earl Moon
| | I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | | This ceramic su
Electronics Forum | Tue Oct 09 14:30:32 EDT 2012 | bandjwet
Put on your Chemical Thinking Caps..... We are ablating the mask of a PCB which was over a copper layer. This exposes copper. Outside of an electrical test (no can do) how could we use a fast non-destructive test in order to determine that copper (
Electronics Forum | Fri Aug 21 14:29:37 EDT 1998 | Earl Moon
| HASL: (hot air solder leveling) is a process used to cover the Cu. Either Sn/Pb is used or Ni/Au or some other combo. In one case you create a land pad and in the other (with resin)you cover the Cu so that you only have a "trace." Is that correct s
Electronics Forum | Mon May 14 14:51:36 EDT 2001 | Brian W.
Personally, I prefer the OSP. I get a flat surface to deposit paste on, resulting in more consistent solder paste volumes. With HASL, the amount of plating and the mounding affect the paste deposition. I have even had it affect the placement. The
Electronics Forum | Thu Jul 09 11:20:24 EDT 1998 | Justin Medernach
| I am looking for a little enlightement with an issue that we have been seeing. We have printed curcuit board with multilayer and HAL finished. | After reflow soldering, we have often "blister phenomenon". | Our reflow profile is normal. Factory