Electronics Forum | Tue Aug 10 15:47:34 EDT 1999 | John Thorup
| | | | | I am having cleaning problems when processing PCB's which have | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tide mark
Electronics Forum | Tue Aug 10 16:01:12 EDT 1999 | Earl Moon
| | | | | | I am having cleaning problems when processing PCB's which have | | | | | | TAIYO solder mask on them. After processing, hand soldering and | | | | | | cleaning, a sticky residue is remains, resulting in a cosmetically poor finish with tid
Electronics Forum | Thu Aug 05 13:03:35 EDT 1999 | Dave Weihrauch
| | | | Has anyone out there tried to parylene coat plastic parts prior to soldering them to a pcb? I'm looking at several potential applications where fewer than 5% of my components on a pcb are plastic, yet from a reliability aspect (environmental
Electronics Forum | Fri Aug 06 07:18:48 EDT 1999 | Graham Naisbitt
| | | | | Has anyone out there tried to parylene coat plastic parts prior to soldering them to a pcb? I'm looking at several potential applications where fewer than 5% of my components on a pcb are plastic, yet from a reliability aspect (environmenta
Electronics Forum | Sat Jul 17 03:02:58 EDT 1999 | Jeff Sanchez
| | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | What is it you're trying t
Electronics Forum | Fri Jun 18 13:55:44 EDT 1999 | Earl Moon
| | Now don't everyone jump on this at once, but it seems time for me to send out copies of my not even close to being dated copy of an article about HASL. Though it was published in 1992, in Printed Circuit Fabrication Magazine, and it got rave revi
Electronics Forum | Mon Jun 14 15:50:07 EDT 1999 | JohnW
| I am looking for more information about: | | 1) What kind of evaluation can I do to measure the resistance to fall off of a bottom side glueded SMT component?; | | 2) There is some influence of doble wave solder machine (temperature, flux, etc) i
Electronics Forum | Thu Jun 03 12:31:30 EDT 1999 | Dave F
| | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Mon May 10 15:49:52 EDT 1999 | Steve Gregory
| | Can anyone tell me what the recommended "typical" cooling rates are after reflow? Are the cooling rates considered as critical to control as the heating rates and why/why not? | | I do not think there is a "typical" post reflow cooling rate out