Electronics Forum | Thu Feb 12 21:30:45 EST 2004 | davef
Comments are: * We're amazed that you can thermocompression bond to epoxy. * Silver may be oxidizing during expoxy cure. * Klein Wassink talks about aging in THE BOOK [Soldering in Electronics: A Comprehensive Treatise on Soldering Technology for Sur
Electronics Forum | Wed Feb 11 09:07:37 EST 2004 | Ashok Thiyagarajan
HI I am currently having a wafer which is stud bumped (Au), I am printing conductive adhesives (with silver fillers) on the pads , and by thermocompression bonding, I am establishing the connnection between. But right now the problem is the silver
Electronics Forum | Fri Aug 23 16:02:37 EDT 2002 | davef
Low Cost Flip Chip Technologies for DCA, WLCSP, and PBGA Assemblies; John Lau; McGraw-Hill Professional; ISBN: 0071351418; 2000 * Chapter 6. Flip Chip on Board with Conventional Underfills. * Chapter 7. Flip Chip on Board with No-Flow Underfills. * C
Electronics Forum | Fri Jun 23 10:10:15 EDT 2006 | Gman
Some amount of voiding was always seen on sites where solder paste is printed. These voids are much smaller. However the site where a flip chip is flux dipped has never had problems with voiding. Macro voids (and huge ones at that)across the board s
Electronics Forum | Tue Jun 29 14:42:55 EDT 2004 | davef
You're correct, for every dumpster full of paper written about solder, there's a sentance written about fluxes. There's dribs and drabs about fluxes in most of the soldering books [ie, Manko, Klein-Wassink, Judd, Strauss, etc] and most of that is ve
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Sun Aug 26 12:40:59 EDT 2001 | stefwitt
I would like to enter the discussion by tossing some numbers in. First of all I don�t like the 3 Sigma value. 3 Sigma are 2000 defects per mio. if I remember correctly. This means, if you have 200 components on the board, then every 10 boards have on
Electronics Forum | Thu May 10 02:57:03 EDT 2001 | kjellman
Hi, Why not have a look at Philips/Assembl�on, their ACM machine is quite nice. It may also bring you down to Flip Chip, 0201 some through hole and odd form placement. Nice options like bulk feeding, coplanarity tests, fluxing for FC, prom feeders (
Electronics Forum | Thu Jul 20 16:08:18 EDT 2000 | Grant Baynham
Do you have any experience with flip chip applications using lead-free solder, and specifically do you have any information revealing how the process parameters for standard air reflow atmosphere can be modified to match the results for solder reflow