Electronics Forum | Wed Oct 23 08:40:20 EDT 2002 | davef

Yer not making this easy. What kind of flux? If no-clean flux, what controls are you using to assure you are: * Applying the correct amount of flux? * Properly activating the flux? If water washable flux, talk to us about your cleaning methods and

Solder and flux

Electronics Forum | Wed Oct 23 07:32:18 EDT 2002 | Yannick

Sorry, the layer is made of flux.

Solder and flux

Electronics Forum | Thu Oct 24 10:05:59 EDT 2002 | Yannick

I don't know the name of the flux. but is a no-clean solder paste.

Wave flux and profiling

Electronics Forum | Mon Dec 18 23:24:50 EST 2006 | grantp

Hi, Yes, I would hate to resort to cleaning, but the product must be clean. We have been using palettes to keep most of the flux off the PCB, but there is still residue around the connectors. Does anyone suggest a good no clean flux to use with le

Wave flux and profiling

Electronics Forum | Tue Dec 19 10:08:10 EST 2006 | George

Grant, Why don't you try a water-base flux which is No-clean, VOC-free also? I have tried the 270WR flux from AIM with good results even on lead-free process. My $0.02, George

Wave flux and profiling

Electronics Forum | Mon Dec 18 14:36:09 EST 2006 | samir

Yikes!! In-line cleaning, to clean cosmetic and benign residues (from a NO-CLEAN) flux... You sure you can't switch fluxes? Another variable with residues is the solder mask. Depending on mask type (glossy, matte, semi-gloss, or semi-matte), will

Solder and flux

Electronics Forum | Wed Nov 06 05:13:01 EST 2002 | Dreamsniper

Crystalline flux if it is really clear should not be a problem. We were using Amtech paste before and we have the same results. Sometimes we mistakenly see it as a dry joint because of the reflections from the lighting of our Metcal inspection system

Wave flux and profiling

Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir

Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll

Solder and flux

Electronics Forum | Thu Oct 24 15:02:16 EDT 2002 | seand

Hello Yannick, Have you brought this concern up with your supplier? I would recommend speaking with your flux and paste provider to gain additional insight and recommendations for resolving the concern. Good luck, Sean D.

Wave flux and profiling

Electronics Forum | Fri Dec 15 18:36:46 EST 2006 | Grant

Hi, I have noticed we are getting residue on our wave pcb's and it's worse with lead free, since we changed to the flux we are using. We are currently using Avantec VOC Free flux model Ecofree 303. It looks like it's made in Malaysia. Does anyone h

  1 2 3 4 5 6 7 8 9 10 Next

flux and sludge searches for Companies, Equipment, Machines, Suppliers & Information

Circuit Board, PCB Assembly & electronics manufacturing service provider

Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
IPC Training & Certification - Blackfox

Reflow Soldering 101 Training Course
best pcb reflow oven

Wave Soldering 101 Training Course
SMT feeders

Software for SMT placement & AOI - Free Download.
Hot selling SMT spare parts and professional SMT machine solutions

Private label coffee for your company - your logo & message on each bag!