Hello, We are bringing online a UP2000 printer and are in need of some squeegees. Can anyone recommend a supplier? This is a used machine so I'm not sure if I would have to register with Speedline if I wanted to order parts from them. I just assumed
Electronics Forum | Thu Feb 19 19:08:02 EST 2015 | comatose
Ignoring the certification issue for a second, what is the alloy of those two joints? The melting temperature? The strength? And no. You added a single homogenous material (leaded wire solder) later in the process. Adding leaded solder makes it non
Electronics Forum | Mon Feb 23 14:58:01 EST 2015 | ercdave1
I found the solution to my problem. Since I don't have a manual for the machine. I had no idea how to change the system settings but by pressing the first 2 buttons on the left of the front panel I got the system settings menu and was able to change
Electronics Forum | Tue Feb 24 06:44:50 EST 2015 | bugarin
Hello , We are using Kester 959T flux and we wish to purchase Aim Ws 716 flux, due to higher activity. We also use humiseal 1a33 for conformal coating. Is anyone using Aim flux and humiseal 1A33, are they compatible ? Thank you for info
Electronics Forum | Tue Feb 24 09:47:45 EST 2015 | rgduval
Well, since you're looking at a water soluble flux from AIM, I'm guessing you wash the boards before you conformal coat them. Thus, I wouldn't expect any interaction between the excess flux that you're washing off of the boards and the Humiseal that
Electronics Forum | Mon Mar 16 11:40:56 EDT 2015 | swag
If it took you a long time to get it through pick and place or you had to do a lot of hand add of SMT parts, your paste can start to dry out especially on the small deposits. We've seen this time and time again. We've gotten way better at quickly p
Electronics Forum | Thu Apr 16 10:11:51 EDT 2015 | hugh_manatee
Your solder paste manufacturer’s profile is just a “guideline.” You can customize your profile to meet your product’s need. For better grain-structure (shiney-ness) try a ramp soak spike profile keeping your preheat temps very low before your reflo
Electronics Forum | Tue Feb 24 16:11:15 EST 2015 | emeto
I assume you have a part number system. If so, you should kit the reel with less parts first from the same part number. If you don't use part number system, then you probably have components sorted by value and size, which should lead to the same pri
Electronics Forum | Wed Feb 25 11:42:29 EST 2015 | emeto
What software do you use to track your parts? We use Manex - it is not perfect but still gives you the opportunity to track parts/jobs relations. For example I know in each moment one particular part goes to 5 currently open jobs. You should explore
Electronics Forum | Tue Feb 24 17:16:11 EST 2015 | grauen06
I was handed the task to develop a process to solder a BGA using topside heat only. It is a long story so I will spare the details, but I was wondering if anyone has ever attempted this? I have been going at it for a few weeks with fair results, but