Electronics Forum | Fri Mar 30 13:06:50 EST 2001 | aortiz
Hi, I need support on the method or applicable standard to measure the shear force strength on chip capacitors and resistors. I know the soldered joints strength is related to land desing, solder volume, pcb and component solderability, component
Electronics Forum | Fri Mar 30 20:06:55 EST 2001 | aortiz
Maybe there's no test and I don't know where or why my customer came with that requirement (I think because in one of the board shipments he got a board were a smd resistor broke, but I think that happened because miss handling), but anyway I need so
Electronics Forum | Tue Apr 03 11:08:21 EDT 2001 | vsorin
Hi, Our engineering board has to decide which technology is better for the hand soldering of the SMT components: HASL or Chemical Ni-Au. We have an automatic line for SMD assembling and our experience shows us that for this automatic line is better
Electronics Forum | Thu Apr 05 22:24:32 EDT 2001 | davef
I think your solder mask is a partial cause of your solder balling. Additionally, adjusting some machine set-up parameters may also help. 1 If we were talking about a single assembly problem, we�d be thinking about the laminate, but since you say t
Electronics Forum | Thu Oct 04 21:52:34 EDT 2001 | sjlevin
If you do not have one of the big in-line aqueous cleaners, then there is an easier way that is a lot less expensive. I suggest you try Asahi's AK-225T vapor degreasing solvent which has been around for 10 years now. And it is legal. If you have
Electronics Forum | Mon Oct 08 21:05:00 EDT 2001 | ksfacinelli
DO NOT Mix Technologies.... If you are using a no clean solder paste use a no clean wave solder process. I have direct experience with using a no clean paste and a RA water-soluble wave solder process. When cleaning with the water wash system your
Electronics Forum | Thu Apr 05 08:36:35 EDT 2001 | jmlasserre
use a solder join temperature of 200/210� whatever the pcb used (tin lead coated or osp or gold fash). 2nd ==> to adapt the temerature to the pcb used: - Reflow (200-210�) for tin lead coated pcb's (in this case we have just to reflow the solder
Electronics Forum | Fri Apr 06 11:37:19 EDT 2001 | raton
We had the same problem years ago when we started using a radial inserter. The inserter would dutyfully insert and clinch the leads. The problem in our case was the component body sealing to the fab, especially on electrolytics caps with a film jac
Electronics Forum | Tue Apr 10 13:43:13 EDT 2001 | mparker
since you did not define what visual process you are inspecting with I will ask is this "grainy" appearance being detected with the naked eye only? Are you using magnification? if so, what power? Is this a SMT solder or through hole solder problem?
Electronics Forum | Wed Apr 11 06:56:20 EDT 2001 | brownsj
Most of the component vendors I've dealt with will guarantee the solderability of the terminations for three years if the components are still packaged in a full reel. If the reel is part used we've kept them for 1 year and then used a wetting balanc