Electronics Forum | Fri Jun 18 15:04:19 EDT 1999 | Scott Cook
| Scott, | | I do hurt easy. Be gentle, at least that's what I tell all the women in my life though quickly diminishing supply - oops. I do not happen to believe this statement. I have seen you dodge many a penned "dart" on this very forum. Since I
Electronics Forum | Fri Jun 18 15:54:29 EDT 1999 | M Cox
| | Scott, | | | | I do hurt easy. Be gentle, at least that's what I tell all the women in my life though quickly diminishing supply - oops. | | I do not happen to believe this statement. I have seen you dodge many a penned "dart" on this very foru
Electronics Forum | Tue Apr 13 13:30:25 EDT 1999 | Cunli Jia @ SMTnet
| After careful consideration, I have come to the conclusion registration, in the manner required to participate in what was an open forum, is not my bag. | | Earl Moon | Dear Earl, We at SMTnet are sorry to hear your decision. You have been a b
Electronics Forum | Thu Aug 24 15:37:50 EDT 2006 | Chunks
Hi Any, This is from an earlies thread "Solder Ball After Reflow Process". Date: August 16, 2006 01:52 PM Author: Russ Subject: Solder Ball After Reflow Process Oven settings are meaningless here. What does the board see? It is the paste we a
Electronics Forum | Fri Aug 25 09:18:40 EDT 2000 | Peter
Welcome back Moon Man. Your title is an apt description of the occurrence of your return. I always enjoy your bombastic baccalaureate, and welcome your feedback and observations. It is very helpful to hear from someone who has reached the point of fr
Electronics Forum | Sun Jun 07 02:06:26 EDT 1998 | Earl Moon
| Earl, | As always, I am interested in what you have to say, but I am still a little vague on your application of ANSI Y14.5 as it relates to the manufacturability of an assembled printed circuit board. Are you implying that component placement coor
Electronics Forum | Mon Nov 27 17:44:10 EST 2000 | Dave F
Gawd. Sure FR-4 will meet those conditions. Tg [check the fine SMTnet Archives for discussion on Tg] of FR-4 is 130�F or so. Consider: * Is the delT between Tg and the upper operating [or storage] temperature acceptable for your application? * D
Electronics Forum | Fri Jul 14 16:29:12 EDT 2000 | Dave F
Awww John, if I typed all that folderol, my spell checker would have gone kaaablewee!!! Most of the stuff I listed is tactical, because I assume most people on the forum are DFM / DFT choir and by the time we get involved, some BIG $$$ consultant ha
Electronics Forum | Fri Jul 14 16:29:31 EDT 2000 | Dave F
Awww John, if I typed all that folderol, my spell checker would have gone kaaablewee!!! Most of the stuff I listed is tactical, because I assume most people on the forum are DFM / DFT choir and by the time we get involved, some BIG $$$ consultant ha
Electronics Forum | Fri Mar 24 17:07:39 EST 2000 | John Thorup
Hello Ashok If you are talking about the thousands of volts that is often generated by either simply unrolling the tape to apply or when it is removed from the board after soldering you don't have a lot of choice since it is an insulator. Ionization