Electronics Forum | Tue Feb 08 15:30:18 EST 2005 | saragorcos
Jay ~ do you have any other contact information for that seminar you are attending concerning the SN100C? I have tried the URL in your message, and it is not working for me. Your help would be much appreciated, and thanks for sharing all your helpf
Electronics Forum | Fri Feb 25 17:53:35 EST 2005 | James
I have the same Heller 1500 and am about to start evaluating paste. Would you be so kind as to provide your oven set points to give me a baseline to start with? I think this would save myself and others a lot of time and effort ;-) Thanks James S
Electronics Forum | Wed Mar 09 12:46:36 EST 2005 | Patrick
MarcA: Could you expand on the results you observed about improved wetting in a nitrogen environment? I am very interested to learn about the impact that nitrogen had. Was there an improvement in the cooling zone with nitrogen? Patrick
Electronics Forum | Fri Jan 21 09:31:38 EST 2005 | clampron
Good Morning Everyone, Does anybody have any information regarding the recommended storage environment for PCB's with tin plating? Any help would be greatly appreciated. Thanks In Advance Chris
Electronics Forum | Fri Jan 21 17:00:10 EST 2005 | Dasalintercept
I don't know what's recommended but I do know that bagging with Intercept eliminates all oxidation in tin parts and platings and the need for dry packaging to boot. Email me if you'd like more information. dasalintercept@hotmail.com
Electronics Forum | Sat Jan 22 14:30:45 EST 2005 | davef
First, your supplier is probably the best source of storage recommendations. Second, storage under proper conditions (20�30�C,
Electronics Forum | Fri Jan 21 11:15:28 EST 2005 | russ
Are you running any type of vibratory wave on the Vitronics as opposed to the electrovert? How about any turbulent wave differences if any? The only time I have ever flooded boards in fixtures is when the seal is broken or run an excess amount of v
Electronics Forum | Fri Jan 21 13:29:35 EST 2005 | vinod
Hi Friends, I had a PCB with polymide material with nickle tin plating on it. I had real hard time to do hand solder. I am asking help if any one have any experience with polymide material.
Electronics Forum | Mon Jan 24 06:15:38 EST 2005 | David
Hi everyone! Is here anyone, who has experience about closed-loop feedback (AOI) with Pre- and post-reflow rework. I need too some internet links, whic handle by this subject. Thanks!!!
Electronics Forum | Wed Jan 26 15:30:00 EST 2005 | JAMES
Universal Sequencer is just a part to tape machine. You will need an inserter inline. But we have a Universal and it works great