Electronics Forum | Wed Apr 09 20:05:21 EDT 2003 | davef
Kevin: We know of no handy approach to developing recipes. * Certainly programs provided by profiler suppliers give you a good first pass, based on your oven and solder paste. * Second pass in developing your recipe comes through trail and error chan
Electronics Forum | Fri Apr 18 08:24:49 EDT 2003 | tsongshe
Hello,all.these days I met many skewed transistors after reflow soldering.we 've tried many ways attemting solving it thoroughly...changing the aperture pattern,solder volume and even changing the size of pcb pad,but the results are not very good.eve
Electronics Forum | Thu Apr 24 20:39:01 EDT 2003 | davef
3NaH2PO3 + H2SO4 + 2H2 + Ni^0 Potassium is co-deposited with the nickel, as follows: H2PO2^- + Hads => H2O + OH^- + P 3H2PO2^- + P => H2PO3^- + H2O + 2OH^- Nick Biunno gives a very short, over simplified summary: "Everybody looks at the nickel, b
Electronics Forum | Mon May 26 08:02:11 EDT 2003 | davef
Resistance: Tables of wire gauge often provide a resistance measure of some kind for each gauge. That way we can estimate the resistance of any length of wire we might be interested in. Calculating trace resistance is only slightly more complicated.
Electronics Forum | Tue May 27 12:40:50 EDT 2003 | davef
Hi Bill You said, "silicon". We assume by your discussion that you ment to say, "silicone". For background on silicone and soldering, check with Dow Corning [517-496-6000]. They make a OS2 [VOC-free] silicone stripper and should be able to give y
Electronics Forum | Tue Jul 15 15:42:34 EDT 2003 | gdstanton
CAL, I'd look into getting some more bids before making a final decision. Try to get quotes from at least four CM. It wouldn't hurt to also consider the core competency of the CM (i.e. High Volume or High Mix). This will give you a better perspec
Electronics Forum | Mon Jun 09 17:53:28 EDT 2003 | MA/NY DDave
Hi My guess is you're from China area, Four Tigers, or Korea. I think you are limiting yourself by only asking for end users opinions, yet that is my long term disagreeably educated opinion. I am going to one of these AOI things this week and mayb
Electronics Forum | Thu Jun 12 13:01:08 EDT 2003 | ServGuy
Yeah, what Techsuppguy said. But further there are a few more points. The first is in the current market situation far less new machine are being purchased and far more are just changing hands. In the past the ratio of warranty machine service pho
Electronics Forum | Thu Jun 26 04:34:49 EDT 2003 | emeto
Hi James, I saw very good posts here.Now I will give you one more practical way: 1. My advice is to encrease the temperature(like your first sidgestion). Termostress is important thing so your first zone should be 120-150C. 2. The paste profile. If
Electronics Forum | Mon Jul 21 20:42:12 EDT 2003 | iman
Don, thanks for the thoughtful insight, can I run some thinking points for your further assistance? 1) ours is a Au over Ni PCB bareboard. Do you think excessive Au thickness is any way a influence for poor solder formation? I did notice the PCB ba