Electronics Forum: glichn and lead and free and wave and solder and lf250 (Page 1 of 4)

lead free platings and tin lead

Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN

I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram

Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS

It may be you should look for higher TG of Durapol Rgds GS

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 22:09:49 EDT 2005 | Ken

My policy is not to mix them. You have zero cross contamination potiental with this policy.

Wave solder pallets: lead and lead-free process

Electronics Forum | Wed Jul 27 16:46:48 EDT 2005 | russ

I don't think that you would need to test these. Have you ever seen any evidence of solder sticking to them? We use the same material and never notice anything besides flux staying on the bottom. Would the lead absorption if any even be of a concer

Solder beads and wave soldering

Electronics Forum | Thu Jul 06 04:41:58 EDT 2006 | Rob

MF300S is quite an old flux, & a lot has happened since then on the flow solder front - are you sure it's designed for Lead free, or is it just a traditional flux that SHOULD work OK with Lead free?

Solder beads and wave soldering

Electronics Forum | Wed Jul 05 10:13:02 EDT 2006 | jdengler

Is the flux rated for lead free? These higher temps will cause most lead rated fluxes to burn off prior to the wave. Jerry

Solder beads and wave soldering

Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds

Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr

Solder beads and wave soldering

Electronics Forum | Thu Jul 06 03:03:56 EDT 2006 | ronalds

Thank you all for your input. The MF300S Multicore flux is rated for lead free. There is not much dross or contamination. We are using nitrogen. I've tested the boards with the curing test of IPC-TM-650. I think you're all right about the preheat.

Wave and Press-Fit fixtures

Electronics Forum | Mon Nov 26 12:00:20 EST 2001 | peterson

Hi everyone, I am looking for a reliable company (preferrably on the west coast) that can make Wave Solder and Press-Fit fixtures for our back-plane division. I need a reliable source that can take our data and produce quality fixtures in a 5-7 day

  1 2 3 4 Next

glichn and lead and free and wave and solder and lf250 searches for Companies, Equipment, Machines, Suppliers & Information

PCB Handling with CE

Software programs for SMT placement and AOI Inspection machines from CAD or Gerber.
SMT spare parts - Qinyi Electronics

Training online, at your facility, or at one of our worldwide training centers"
SMT feeders

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...
2024 Eptac IPC Certification Training Schedule

Component Placement 101 Training Course
SMT spare parts

Thermal Transfer Materials.