Electronics Forum | Mon May 24 13:42:40 EDT 1999 | David M. Lynch
I was doing some digging for comments from folks like yourself and noticed your mention of Amistar, Philips, and Transition Automation service. As it happens I'm comparing Amistar and Philips machines and support. It's obvious why you're happy with P
Electronics Forum | Wed Jul 15 10:37:58 EDT 1998 | Ben Salisbury
| | We just have a use cp4 .I have a problem on transfering data between cp3 to cp4 .when I use the data for cp4 I can't have parts in correct location. Is that normal? or it's because that has a different vision system.if so.how can i do with it.the
Electronics Forum | Sun Jul 12 01:23:38 EDT 1998 | Mike Cox
| There's a company out the that makes air sleds for moving equipment around. Air sleds are heavy duty plastic plastic bags with lots of little holes in the under-side. The bag is positioned under the equipment. A vacuum cleaner, hooked-up backwar
Electronics Forum | Fri Jul 10 09:17:13 EDT 1998 | justin medernach
| There's a company out the that makes air sleds for moving equipment around. Air sleds are heavy duty plastic plastic bags with lots of little holes in the under-side. The bag is positioned under the equipment. A vacuum cleaner, hooked-up backwar
Electronics Forum | Thu Jul 09 11:32:16 EDT 1998 | Justin Medernach
| What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joi
Electronics Forum | Mon Jul 06 17:42:49 EDT 1998 | Bruce Houghton
| I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built some
Electronics Forum | Thu Jul 02 14:46:34 EDT 1998 | Steve Schrader
| I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built some
Electronics Forum | Tue Jun 30 09:31:36 EDT 1998 | Earl Moon
| The SMTnet Forum archive listings are now available for public inspection. You can post messages from the archived messages, but it will not place your message in the archived listing. Instead, your message will be placed as a _new_ thread at the t
Electronics Forum | Thu Jun 25 18:17:26 EDT 1998 | Earl Moon
| What is the industry standard for calibration compliance certification of SMT machines? and Flow Solder machines? | We are currently doing a Quality Audit on one of our manufacturing venders and this questions has been brought up. | Any help would
Electronics Forum | Thu Jun 25 15:33:51 EDT 1998 | Earl Moon
| | Hi there, | | Does any one know what is TCE for fully wet saturated FR4. I came to know that for Dry FR4 the TCE is about 15-19 PPM �C. Is that true? | | | | Appreciated for your help. | | rgs, | | chiakl | Chiakl, | It looks like you are speaki