Electronics Forum | Mon Sep 12 14:38:56 EDT 2005 | patrickbruneel
Amol, Your problem is already very isolated only one part has the problem (the part that is hand soldered) Manual cleaning is very difficult. Why are you not considering a no-clean cored solder to solder the one part and skip the manual cleaning. Do
Electronics Forum | Thu Sep 15 13:52:40 EDT 2005 | pr
We had 2 at my last company. As I recall we had a hell of a time with bad blower motors. I'm not sure how you'd check on that, but maybe that problem has been fixed by now (it's been a few years). good luck, pr
Electronics Forum | Fri Sep 16 12:58:49 EDT 2005 | vikkaraja
Fuji sells a PAM kit. It includes all the needed things you will need to accomplish this. It has a reel of 1206 black colored chips, doule sided tape, PCB, flopy with PAM program , and a ram card for the particular machine. I hope it help you some. G
Electronics Forum | Thu Sep 22 06:12:05 EDT 2005 | gavinscott
Hi All, I have been tasked with a project on the control of moisture sensitive devices and I was hoping to get some input from the experts out there... How do you monitor total exposure time for a MSD? If the packaging has been opened and re-sealed a
Electronics Forum | Thu Oct 06 00:41:56 EDT 2005 | vinitverma
Hi, If you're thinking of a new machine and the volumes are not very high, I think Assembleon's OPAL XII should be the best fit. It can handle VERY LARGE boards upto 25.5" x 17" (with single pass) and 25.5" x 33.5" (with double pass). However for th
Electronics Forum | Mon Oct 03 17:57:36 EDT 2005 | Andrea
I am wondering if anyone can direct me to some resources that would help my team define some ispection criteria for silver epoxy. We are using the epoxy on joints as little as 0805. My team has differing opinions on how much is too little and how muc
Electronics Forum | Thu Oct 06 09:27:54 EDT 2005 | Amol
measure the board thickness before coat by a screw gauge, and then after, when the coating has fully cured. this works well for a single side coat. once your wet to dry thickness is down, you can spray to a particular thickness wet and be reasonably
Electronics Forum | Mon Oct 10 22:29:04 EDT 2005 | matjen
We are trying to place a connector with a IP2 but every vision # we have tried will not place the connector, If anyone has any flexa experience or knows a vision # that we can enter in that will place a odd shaped connector please let us know, Th
Electronics Forum | Thu Oct 13 14:14:10 EDT 2005 | rcanten
It depends on the type of connector but if you have a connector that has projections on the ends that look similar to leads in the lighting you will be hard pressed to get this to place with anything other than a vision number 6 on a IP2 and then the
Electronics Forum | Wed Oct 12 12:33:11 EDT 2005 | Inds
Hi Everyone, I am trying to site dress PTH holes filled with Nihon solder mixed with SAC solder at the rework station. But what i am seeing is the solder just doesn't melt and I am not able to suck the solder out of the PTH. Has anyone faced this i