Hello Ed, I have and run a 4683a ofs. If you have any questions I may be able to help. Steven Curd Sr. Engineer Hitachi
Electronics Forum | Tue Jul 18 14:21:01 EDT 2000 | JAX
Jeff, I would tend to agree but then again I am not an expert. Get in touch with technical support at following link. They will probably need a little more info but they should have an answer. Have Fun!
Electronics Forum | Fri Oct 06 10:59:02 EDT 2000 | Peter loten
the IRSI may well be quicker on your first board, but the CR6520 will be quicker once you've built up a raesonable component library. Don't forget - you may have to re-programme the IRSI every timeyou have small component changes such as date codes
Electronics Forum | Wed Jun 28 12:29:59 EDT 2000 | Christopher Lampron
Does anyone know what the min-max plating thickness for HASL is? Is there a specification that defines this requirement? We have had problems with PCB's that have excessive solder plating on the pads. This wreaks havok with our QFP's. Any help would
Electronics Forum | Wed Jun 28 12:29:56 EDT 2000 | Christopher Lampron
Does anyone know what the min-max plating thickness for HASL is? Is there a specification that defines this requirement? We have had problems with PCB's that have excessive solder plating on the pads. This wreaks havok with our QFP's. Any help would
Electronics Forum | Thu Jun 15 08:10:14 EDT 2000 | Dave A
Gary, Have you looked at Cimetrix Inc.? They have several packages dedicated strictly to CIM. I think you will be happy with it. Website is www.cimetrix.com Check it out and let me know what you think. Thanks, Dave
Electronics Forum | Thu Jun 08 17:10:22 EDT 2000 | pgarsoe
The link to the paper from the following page in your library: is dead. I have been unable to obtain any response from my attempts at registration, so in my frustration have decided that maybe you guys oughtta at least know about it. Regards, Steve
Electronics Forum | Wed Jun 07 13:23:10 EDT 2000 | John
I intend to evaluate a Wave Rider in our process in the next couple of weeks. I don't think I would appreciate the continual maintenence of the device. Does anyone have any experience with the Optimizer product? Does it have similar issues? Thank
Electronics Forum | Tue May 30 10:46:06 EDT 2000 | Travis Slaughter
Sounds like you could have a problem caused by the gold. How thick is the plating? Are the connector leads gold too? I have seen gold cause dry looking brittle solder joints in the past.
Electronics Forum | Sun May 21 10:39:35 EDT 2000 | Jan Rinaldo
Does anyone have experience with this machine? I'm having some troubles with it. Recognition system is the most critical of them. Thanks in advance, Jan