| | | We are currently using a 65/35 solder for our wave process but are considering switching to a 63/37 for a substantial cost savings. No one here seems to know why we everused a 65/35 formulation in the first place. | | | I understand 63/37 to be
Electronics Forum | Wed Feb 03 18:32:07 EST 1999 | Earl Moon
| I'd like to find some technical papers on the reliability of reworked BGAs. If you know of any, please let me know. | | I have a concern about this because our current rework process does not apply solder paste to the pads prior to placing the pa
Electronics Forum | Thu Feb 04 15:44:04 EST 1999 | Michael Allen
Actually, solder paste adds about 12% to the joint volume for PBGAs, or about 31% for MicroBGAs -- assuming standard (recommended) pad sizes and stencil thicknesses, and paste with 90% metal content (50% metal by volume). | | I'd like to find some t
Electronics Forum | Sun Jan 31 23:03:57 EST 1999 | Dennis O.
| | hi, | | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier pr
Electronics Forum | Thu Jun 04 11:23:25 EDT 1998 | Justin Medernach
| What methods do people use to dress pads after removing and before replacing the BGA? | We use solder wick and a soldering iron, focusing on not "dragging" the wick across vias. This is laborous and booring. Who has a better way? | Dave F Dave, Her
Electronics Forum | Sat Jun 06 07:04:27 EDT 1998 | Dave F
| | What methods do people use to dress pads after removing and before replacing the BGA? | | We use solder wick and a soldering iron, focusing on not "dragging" the wick across vias. This is laborous and booring. Who has a better way? | | Dave F | D
Electronics Forum | Thu Jun 04 22:36:23 EDT 1998 | Dave F
| | What methods do people use to dress pads after removing and before replacing the BGA? | | We use solder wick and a soldering iron, focusing on not "dragging" the wick across vias. This is laborous and booring. Who has a better way? | | Dave F | D
Electronics Forum | Mon Mar 30 16:39:04 EST 1998 | Tony Arteaga
Hello there, I am currently doing BGA repair and basically I am applying the same process as Mike sujested. It is actually the way to go when creating a profile. The next process is re-balling your package, that is if you whant to use the same compon
Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Mon Aug 28 17:04:52 EDT 2006 | Board House
ImSn - Immersion Tin - Not Recomended- short shelf life ImAg - Immersion Silver - Prefered Surface finsh by most Board houses, Best reworkablility, 12 moth self life, ENIG - Electroless Nickel Immersion Gold - Second Choice for Board Shops, 12 -