Electronics Forum | Tue Dec 16 19:45:47 EST 2003 | Hiram
Hi, I am looking for the IPC criteria hole-to-lead ratio. Does anybody know a practical way to determine if some holes in my pcb's do not get enough solder in the wave solder machine because an inapropiate hole-to-lead ratio? Thanks in advance! Hi
Electronics Forum | Wed Mar 10 18:42:34 EST 2010 | 89jeong
Hello Sir. We also encountered the same pin-hole issue but there was around MLCC.I also looked for some information in technical report and internet, But i failed to get an answer. As you know this pin hole or blow hole is caused by the solder boilin
Electronics Forum | Wed Dec 17 09:53:26 EST 2003 | davef
IPC-2222 - Sectional Design Standard For Printed Board For Organic Printed Boards, Table 9-3 � Plated Through Hole Diameter To Lead Diameter Relationships will give you the standard information you require. If we can�t get proper hole fill after try
Electronics Forum | Mon Sep 14 08:07:24 EDT 2009 | davef
You have a board fabrication defect. Search the web for "hole wall pullaway" Performing a microsection is the best way to analyze the defect.
Electronics Forum | Thu Mar 11 03:03:26 EST 2010 | grahamcooper22
Hi , Looking at your photo....can I also see a hole in the middle of the joint on the chip component ? Maybe its not just a problem with th ejoint son diodes ? Did you also get mid chip solder balls on chips? If so, I'd almost guarantee the pcb has t
Electronics Forum | Wed Dec 17 10:10:35 EST 2003 | Hiram
Thanks Dave, your comments were very helpful! Hiram
Electronics Forum | Thu Mar 11 02:56:01 EST 2010 | grahamcooper22
Hi, blow holes / pin holes / holes in joints are usually a sign that there is excess moisture somewhere around the solder joint. Moisture can be in pcbs / components, so try drying them....a simple thing to do is pass a bare pcb throught your reflow
Electronics Forum | Sun Sep 13 19:56:21 EDT 2009 | 89jeong
Hi All I have a pig problem after reflow. It is a blister in hole.It happend after reflow(Lead free solder) I touched the blister with tweezer. The plating was lifted off easily How do i do? What is a root casue? Drilling or plating? Is it possible
Electronics Forum | Tue Mar 09 20:50:40 EST 2010 | jkhiew
We have encountered high percentage of pin holes issue after lead-free reflow soldering from particular diode supplier that manufactured at Morocco. However, very little reject being found if the particular component is manufactured at China by using
Electronics Forum | Fri Sep 18 09:22:03 EDT 2009 | ysutariya
Don't forget the possibility of excess moisture absorption. If this is lead free, then the laminate manufacturers state that you should bake prior to assembly. Was this completed?