Electronics Forum | Tue Aug 22 13:05:32 EDT 2006 | Board House
Hi CP, From a PCB manufacturing side, all of our product is Lead free / RoHs compliant if it has a surface finish other than Hot Air. To be ROHS compliant and Able to with stand Lead Free Assembly, this is where the board house would need to switch
Electronics Forum | Fri Mar 21 15:51:23 EDT 2008 | g2garyg2
Thought I would reply and try to assist. PROMATION, my company, also manufactures Diode Laser soldering systems but with this stated we also manufacturer iron tip systems, soft beam systems and hot air solutions. The reasons are simple. Diode Laser
Electronics Forum | Wed May 16 15:40:56 EDT 2012 | davef
Here's some notes from a Bob Willis presentation Assembly of Flexible Circuits with Lead-Free Solder Alloy [Bob Willis leadfreesoldering.com] * Flexible Circuit Construction ** Base Material - 0.05mm Copper 18/18 um ESPANEX from Holders Technologies
Electronics Forum | Tue Sep 18 20:01:46 EDT 2012 | vergara1
Thanks for the advice. We have only done one PCB > with HMP solder and did not use preheating, but > I've been wondering if it would have been helpful > since we had some trouble getting the solder to > flow. If you have any more specific advice
Electronics Forum | Fri Sep 24 10:57:18 EDT 1999 | Earl Moon
| Hi Folks: | | We've been having bridging problems on our fine-pitch QFP's, despite thorough inspection of paste height, volume, and placement accuracies....profiles look good also. | | The bridging is happening after coming out of reflow...one la
Electronics Forum | Thu Aug 19 22:59:48 EDT 1999 | Jeff Ferry
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad
Electronics Forum | Thu Aug 19 23:56:49 EDT 1999 | Earl Moon
| | I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the
Electronics Forum | Fri Aug 20 09:33:51 EDT 1999 | Don Morgenstern
Earl & Jeff Our machine is different than the Electrovert Solder Pak in that it is does not behave like a "volcano". Jeff, please contact me if you have safety concerns as perhaps you also want to consider our equipment. | | I'm trying a second ti
Electronics Forum | Fri Aug 20 13:00:16 EDT 1999 | ScottM
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad
Electronics Forum | Thu May 20 07:53:55 EDT 1999 | Chris Nuttall
| | We care currently running into problems during our plug via process: | | At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.Thi