Electronics Forum | Wed Dec 22 07:20:21 EST 2010 | piter
HI I used both of solder leveling HASL and ENIG, HASL I can recommended for biger pitch is cheaper solder leveling than ENIG but problem with that solder leveling is during the reflow process HASL isn't flat and during reflow process component move
Electronics Forum | Mon Dec 20 16:22:45 EST 2010 | rkondner
When you say Fine Pitch is this .5mm or is it smaller? I wonder what problems they experienced with HASL, the only problem I recall hearing was the surface was not flat. When applying paste with a stencil I can not see how the flatness is an issue.
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Tue Dec 21 12:28:27 EST 2010 | wrongway
I know when we used them we had problems when one pad is 7 mils tall nest to a flat pad one lead touches the pad the lead next to it isnt touching anything so then have an open I don't see how anybody dosnt have problems with it that use quad flatpa
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Tue Apr 17 10:16:42 EDT 2001 | davef
Welcome to SMTnet. Awww, those assemblers are always whining about something. Just tell him to shut-up and build the blankin� boards. Jeesh!!! We used to have copious archives on the topic on SMTnet and our friend Brian is working his fingers t
Electronics Forum | Fri Oct 14 09:58:13 EDT 2005 | patrickbruneel
Here's what I believe is happening. The main difference between the HASL boards and the gold plated boards is that HASL boards are pre-soldered. HASL boards need very little flux activity to get good hole fill and the machine settings have a wide pro