Electronics Forum | Tue Jun 28 13:04:08 EDT 2005 | slthomas
Are you saying that increasing the frequency of cleaning to every 3 boards *reduced* bridging, or that it's just something you tried? I don't understand why that would help(in my experience it has reduced "insufficient solder" conditions but not brid
Electronics Forum | Wed Aug 10 17:19:24 EDT 2005 | Steve Stach
The propensity for flux residues to cause shorts can be increased in humid environments where water molecules hydrate the surfaces. At high frequencies, electrons travel on the surface of conductors/insulators, increasing the likelihood of shorts in
Electronics Forum | Mon Oct 03 19:15:32 EDT 2005 | cn
is this a single brd or multi up array? What is the thickness? where were the brds made, state/country? I had an issues with a brd which was fabed in mexico during the humid months there was mosture trapped in the brds which caused many strang things
Electronics Forum | Fri Sep 30 10:08:50 EDT 2005 | pete_d
What types of tests are performed to help evaluate solder integrity in the field over a length of time (say about 10 years)? I was thinking humidity tests, temperature cycling tests... but I don't even know what standards to test to. I want to tes
Electronics Forum | Fri Dec 16 11:21:18 EST 2005 | patrickbruneel
Steve, Water-soluble fluxes are per definition very corrosive and need to be cleaned (read the data sheet) Encapsulation will prevent humidity reaching the water-soluble acids but will not prevent reducing the metals the flux is in contact with to m
Electronics Forum | Thu Jan 12 17:35:34 EST 2006 | russ
We use immersion Silver for all of our lead free PCBs. They come in the "silver saver" paper you speak of and we have found that they will tarnish after 7 days in the open enviroment. Even with this tarnish we experienced no reflow problems. We are
Electronics Forum | Mon Jan 09 05:14:56 EST 2006 | abhinavajmera
Hi all, I want to know the possible causes of poor paste release in stencil printing process if the same brand and part number of solder paste that has been used successfully is being used with a set of process parameters which worked before. Other t
Electronics Forum | Tue Jan 24 21:07:17 EST 2006 | davef
We all genuflect to Graham Naisbitt, a generous contributor to SMTnet. Moisture-curing urethanes may form minute bubbles if the coating is too thick or the coating environment is too humid. So, tell us more about your urethane and the method you u
Electronics Forum | Fri Feb 17 17:26:56 EST 2006 | mika
Hmm... how about the people inside this room; working in this dry environment? This is something never discussed highly, but I believe it is most certainly important for the human health. This is another interesting thing about RoHS; the side effects
Electronics Forum | Sun Aug 27 20:30:53 EDT 2006 | darby
AJ, We use all ENIG boards. After opening, any remaining boards are kept in low humidity keeping cabinet. I have never experienced a problem using this method I think the longest I have kept them this way is eighteen months. We also store any open tr