Curious PCB technology

Jan 30, 2020 | Clever idea. I used to work on hybrids. baking temp about 850 degrees C we used titanium and ceramic

Ceramic PCB Challenge

Jul 18, 2018 | Thank you for your response and information. I don't have any idea on what is Hybrid Circuits but i

Ceramic PCB Challenge

Jul 18, 2018 | If you mean hybrid circuits, it is an entirely different discipline! Try this website:- http://ww

Thick Film Screen Printer

Aug 15, 2016 |

Vacuum Soldering

Jun 12, 2014 |

Flex pcb carrier / palett

Dec 2, 2012 | A few years back when I was working in a Hybrid company we used carriers machined from aircraft grad

Sn62Pb36Ag2

Nov 30, 2010 | 62/36/2 is used often in thickfilm hybrid circuits where Pd/Ag conductors are used. The idea is tha

BGA Voids

May 21, 2010 | iv40, Thanks. The PCB that we are populating the BGA hybrid onto does not have holes in the vias

BGA Voids

May 21, 2010 | Erli, Thanks for your feedback. The BGA hybrids were baked before production. I had a particula

BGA Voids

May 19, 2010 | Hello, I'm having problems with voiding on an assembly that has a GPS hybrid with balls much like

SAC BGA in Pb Process

Mar 29, 2010 | SAC 305 liquidus is 219 C. A hybrid profile is often recommended with a peak of 230 C (reflow the S

Pb soldering to Pb free finishes

Oct 5, 2009 | this is what they call hybrid soldering....i missed the discussion at the IPC Show in Chicago...

PBF BGA or PB BGA

Dec 4, 2008 |

Ekra Stencil Printer

May 16, 2008 | Hi There is a Benchtest on the EPP Stand at the SMT Hybrid & Packaging exhibition that may be on in

Pb-Free BGA on SnPb Assemblies

May 8, 2008 | I am with Rwyman. This "hybrid" profile is also used for reworking the BGA's.

Sealing Clips

Mar 26, 2008 | Sealing clip, clamps used in semiconductor, hybrid packaging * Connor Manufacturing Services; 16233

Tombstone/ Poor welting

Feb 20, 2008 | Pd/Ag doesn't usually dissolve (leach) nearly as bad as Ag only. In my hybrid days, we would use 62

BGAs not reflowing??

Nov 6, 2007 | Tony, search the archives for "hybrid profile". There's alot of good info. in there about running L

double printing

Mar 20, 2007 |

Hybrid Profile

Nov 14, 2006 |

Hybrid Profile

Nov 13, 2006 |

Hybrid Profile

Nov 12, 2006 |

Component Peel Strenght

Oct 16, 2006 |

does potato can absorbed the solder or lead

Jul 15, 2006 | Yeah, when all those hybrids need their batteries replaced we can load them up with spuds...

Palladium poor wetting

May 23, 2006 | They work well in silver conductive epoxy in hybrid applications. They are very poor in no clean ap

Apr 18, 2006 | Did you try tensile testing after thermal cycling? If there are any intermetalic problems between th

Apr 15, 2006 | Amol, We pulled off this "hybrid profile" with a leaded solder paste. We recently got our tensil

Apr 14, 2006 | As from previous discussions on this topic here on SMTnet, we are perfectly comfotable using leadfre

Apr 14, 2006 | Hi, I am in the process of developing a "hybrid" reflow profile to solder a board that has LF BGAs