Electronics Forum | Wed Aug 18 15:52:21 EDT 1999 | DENNIS FOWLER
| | | Gian | | | | | | You alarm me when you talk of white residues in a "no-clean" process. This should not happen. It sounds like you have compatibility problems between different residues and/or a poorly polymerised solder mask. | | | | | | Ther
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc
Electronics Forum | Fri Feb 11 01:36:22 EST 2005 | brown
OK I am counting someone knowing this. True or False, if my touch-up operators touch-up the smt solder joints too many times will this make the joint weaker? if yes why? and what happens to my intermetalic layer? I have insisted if it looks good don
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c
Electronics Forum | Tue Aug 10 05:51:03 EDT 1999 | Gian.D
| | hello to everybody, | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | does anybody know how to eliminate flux residues or how not to produce them during rework op
Electronics Forum | Fri Feb 11 08:15:35 EST 2005 | davef
It sounds like you already know the answer. Hand soldering is much more stressful to a board than mass soldering, because: * It is more localized and there is no preheat. * It is more difficult to control. [Different connections require different h
Electronics Forum | Fri Aug 10 18:17:43 EDT 2018 | tey422
I am sorry to hear that they are unable to help you out too. If you do came up with the doable solution later, be sure to let me know about it too. I would like to learn new trick or knowing which house that can handle such task.
Electronics Forum | Fri Aug 10 16:01:51 EDT 2018 | ks0707
Hi Thomas, Thank you for your advice. BTW, unfortunately, I received negative answer from the Fixture house same as below. =========== We have an issue here. Your board is too thin. It is fine to make the fixture for first side. But when you run