Electronics Forum | Thu Sep 02 16:12:51 EDT 2004 | Mike Konrad
Hi -K We are a manufacturer of ionic contamination testers (not yours). In most cases, automatic mode is appropriate. In some instances however, you may need extra time to �release� entrapped contamination from the sample. Automatic mode is not a
Electronics Forum | Fri Nov 26 02:49:46 EST 2004 | Mike
Help! I have a small SMT section that produces low volume but high mix assemblies and, therefore, has over 300 devices. I am looking for a low cost flexible storage solution and believe I have an idea which I recall is available but I cannot find w
Electronics Forum | Thu Feb 10 09:30:32 EST 2005 | cyber_wolf
I am curious as to why you are using Koki ? Why are you not using a main stream paste that is proven in the industry? Indium,Kester,Multicore,AIM.... It has been my experience that when you start having paste-releasing problems out of the blue, it
Electronics Forum | Thu Mar 03 09:04:26 EST 2005 | russ
Been following this thread and have a question, Why do "touch-up" people follow different criteria than "Q.C." people. It sounds like the root of the problem is not addressed but bandaids are being put into place. We have no "Q.C." department and
Electronics Forum | Tue Mar 22 07:39:05 EST 2005 | davef
There is no standard. This is a relative test. If you wish to do tests of this kind, we suggest to pay attention to the following points: * Shear strength of soft solder depends on the deformation speed applied. The faster the material is deformed t
Electronics Forum | Mon Apr 04 09:45:55 EDT 2005 | Homer
IPC may help, otherwise there are many factors: Are the PTH clinched or straight? If straight, what length protrusion? What direction are the parts running thru wave? Is product on a pallet? Not to mention your soldering process: What type of mach
Electronics Forum | Fri Apr 15 10:47:09 EDT 2005 | patrickbruneel
Dhanish, If I understand correct your ICT doesn't detect shorts and only measures capacitive and resistive values. The webbing as Ken mentioned would have a resistance because this is caused by a lack of flux and the web is mainly tin oxide, which w
Electronics Forum | Wed May 04 09:37:08 EDT 2005 | MikeaJ
I would not recommend trying to cram or mix and match multiple images on a stencil. Especially if you are a contract house, and your clients don't understand why sending one board seperate from a panel of four is a pain in the face. However, I have h
Electronics Forum | Fri Jun 30 03:38:21 EDT 2006 | fastek
Things are changing and I think you will see more product coming back to the US as we go forward. China is seeing massive wage increases and the cost of living/housing is becoming over heated. The wage advantages they had over everyone else is quick
Electronics Forum | Wed Jun 15 16:54:33 EDT 2005 | linny999
Siemens is an excellent platform. To reduce your scrap:- Carry out the specified maintenance, especially the segments and valve plungers; Calibrate revolver heads to benchmark. Remove the tables, smooth the magnetic strips, clean the mounting faces,