Electronics Forum | Mon Jun 26 08:08:32 EDT 2006 | davef
It does make you think the immersion coating is causing the voiding, doesn't it? We never have seen that.
Electronics Forum | Fri Jul 09 18:36:48 EDT 2010 | rway
We don't use flex pcbs but have the same issue here. Most of our pcbs are HASL finish. I have looked at silver and gold immersion and both look really good under my color camera on my AOI. However, gold is more pricey. There is no additional cost
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Mon May 14 17:12:20 EDT 2001 | davef
Continuing along the path that Brian took ... IPC-7525 gives design guideline for stepped stencils. It goes something like: * Stepped area SB GT 25 thou from pads located on the greatest thickness of the stencil * Pads in stepped area SB GT 35 tho
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Thu Jun 29 10:11:06 EDT 2000 | John Thorup
Hi Bob, welcome Let's take this a little further. You'll also see HASL referred to as HAL and gold referred to as ENIG (electroless nickle, immersion gold. Other common surface finishes for preserving solderability include OSP(organic suface protect
Electronics Forum | Fri May 10 12:00:41 EDT 2002 | genny
It seems like the biggest problem with silver is its availability. With only a small number of companies offering it, that affects lead time and price. However, everyone I've heard using it seems to think it is excellent. No one seems to have a go
Electronics Forum | Mon May 13 11:17:57 EDT 2002 | genny
I think for our company, the reason we have not yet tried it is two fold. One - we are just barely starting to see a need on a new product under design for a flat finish, so currently we don't use any of the really flat finishes available. Two - Silv
Electronics Forum | Sat Aug 22 15:12:32 EDT 2009 | rossi
Thank you for replying. 1) the finish is Gold Immersion (ENIG) 2) paste type EM907 SN96.5/AG3.0/CU0.5 3) it is always the same BGA but its not on the same ball every time. It is always at the joint on the PCB pad like the solder is not sticking prope