Electronics Forum | Thu Mar 10 13:05:41 EST 2005 | patrickbruneel
This phenomenon is caused by a high amount of halogens (Cl, Br etc.) used in the flux activators or in the flux surfactants. We've seen effects creating all colors of the rainbow. Changing to No-Clean (halide-free) will eliminate this color effect.
Electronics Forum | Thu Mar 10 14:31:57 EST 2005 | russ
Patrick told you why, But here is some more info for ya, I would absolutely not recommend that wires be tinned with OA. The residue will never get cleaned underneath the insulation and all of your strands will strt to break in the near/far future.
Electronics Forum | Thu Mar 10 10:06:08 EST 2005 | steve
OK all you Gurus here's one for ya. Customer is tinning wires with standard eutectic solder in a solder pot. There is a blue tint to the solder in the pot. After tinning with OA flux, which I will change to NC shortly, he has clear teflon insulation
Electronics Forum | Thu Mar 10 15:43:06 EST 2005 | steve
Thank you both for your assistance. I knew that I could count on you folks. The customer has purchased No-Clean flux and is using it as we speak. Hows that for customer service.... All in a days work... Thanks again You make me look good!!! Steve
Electronics Forum | Thu Nov 02 04:42:48 EDT 2023 | tinaheussaff
In general, it is safer to use a single alloy with a known composition and performance characteristics. If you need to change the alloy used in your selective soldering machine bath, it is advisable to consult with the manufacturer or a soldering exp
Electronics Forum | Tue Oct 18 10:36:46 EDT 2022 | winston_one
Dear proffessionals! Question is about this alloys - Sn99Cu07 and Sn100 (Sn100C,Sn100Ni+ etc.). Is it O'k to mix them? In my case to use Sn99Cu07 as addition to selective soldering machine bath with Sn100C? Main components are the same, but minor add
Electronics Forum | Mon Feb 19 11:36:39 EST 2001 | billschreiber
Hello Mark, I wish it were that simple so I could direct you to a particular manufacturer and stencil cleaner model. Unfortunately, there are several issues complicating the process of cleaning all these applications in one machine. First and fore
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
.gif)