Electronics Forum | Tue Sep 17 06:43:00 EDT 2013 | dancingbear1965
9) Not sure if you ever got an answer to this. Where are you based as Pillarhouse offer free training if you visit them. For USA they are in Chicago and for UK they are just outside London. They also have plenty of documentation they can provide FOC.
Electronics Forum | Tue Oct 16 10:39:35 EDT 2012 | trottmann
Hello, are you useing any Through hole AOI in your conventional Hand Assembly and what Typ is it pre- oder post-solder? And what errors are you ecpecting to detect? -missing component -component Offset -polarity Check -or??? Is there Any Manufactu
Electronics Forum | Tue Oct 23 05:58:50 EDT 2012 | trottmann
Does anybody have experience with "DCB Automation - UltraVision"? It looks like an good equipment, but user Information are very rare based on www
Electronics Forum | Tue Oct 16 13:33:16 EDT 2012 | sarason
There was another thread on this recently. But in answer to your question the manual placers are at least half as slow as a container on the desktop and the board sitting in front of you. sarason
Electronics Forum | Thu Oct 18 16:58:01 EDT 2012 | dontfeedphils
Does anyone know if there is a way to adjust the tolerances in the software to decrease the temperate window that the cells will turn green on Heller's V1.0.xx software (running on a 1800)?
Electronics Forum | Mon Nov 19 05:37:21 EST 2012 | eniac
Good table, but I think that first of all - this is data-sheet from manufacturer of your capacitors. This part of web-site (about capacitors) - just a basic information, which we need for a common understanding.
Electronics Forum | Mon Oct 22 16:47:09 EDT 2012 | edmundo
We use a NC Flux in the wave solder and after aAcelerated Life Test cicle we found contamination white residues paths between some solder points. Does somebody know a possible cause for this contamination.
Electronics Forum | Tue Oct 23 10:41:36 EDT 2012 | blnorman
Ideally first you need to analyze the residue to see what it is. We had a customer with white residues after wave and elemental analysis revealed tin.
Electronics Forum | Thu Oct 25 06:45:52 EDT 2012 | mccabekev
I have read through the IPC/JEDEC J-STED-033.1 standards regarding bake and storage of MSDs. The lowest bake in the standard is
Electronics Forum | Thu Oct 25 11:15:55 EDT 2012 | aj
are you sure the zone 5 blower is running? sounds like it isnt.... no harm to check all blowers while you are at it.