Electronics Forum | Mon May 02 15:36:40 EDT 2011 | marcpeo
One more note on this. The techs tell me that the main reason for the PV immediately matching the Set Point is that the software is in "Edit Mode". This is a mode that allows one to iterate the software without the oven running. That might also ex
Electronics Forum | Thu Apr 28 17:02:07 EDT 2011 | grasso1976
Has anyone had success utilizing the lifted lead/ height checker feature on a Mirtec MV-7L. We recently had two separate events where the machine did not detect a lifted lead using the ic/bridge inspector. The soldering results came back with out def
Electronics Forum | Thu May 05 08:14:45 EDT 2011 | kahrpr
Where black pad exists, it is not a common problem. When I read it is totally random I doubt that. You have defiantly something going on that is unique with the process. It is either your board manufacturer or your solder paste or your profile. It c
Electronics Forum | Fri Apr 29 19:39:58 EDT 2011 | jbaez1
Hi, have somebody out there experienced problems picking up passive components with flexjet head FJ7P?? Just 1 nozzle-spindle is failing, trying to pickup a resistor,cap or diode; I have already changed nozzle tip, nozzle adaptor including springs,va
Electronics Forum | Thu May 12 18:32:02 EDT 2011 | jbaez1
Also... this is ONLY a pick issue? No issues with > placement for those that you do successfully > pick? > > Have the spindles been calibrated > lately? Hi Vickt! thanks for your comments,,during step mode no failure at all, the spindle moves d
Electronics Forum | Tue May 03 17:59:19 EDT 2011 | jimlas53
As I continue to add more components/feeders to our assembler, I add a new laser align extent for every pick. But if components are standardized (like 0805, SOT-23) is it necessary to have all individual extents or just an extent for each type? Thi
Electronics Forum | Wed May 04 21:32:30 EDT 2011 | jimlas53
Thanks for the answer, RLM, I couldn't find anything in the manual that was helpful. If I use a common extent for each component type, I need to identify those components that may be turned due to the feed type (tape, vibe). Is this where I would d
Electronics Forum | Thu May 05 11:11:20 EDT 2011 | jimlas53
OK, understood. In the case of SO14, I have some in vibe feeders and some in tape. The tape parts, when I set the extent up, would be picked at 0 Theta, because the part length is parallel to the Y axis. The vibe parts, which are perpendicular to
Electronics Forum | Wed May 04 06:06:34 EDT 2011 | clampron
Good Morning, I have been working with a company that has a selective electroplate touch up system from Rapid Electroplate. They have used this for repairing gold electroplate. Scratches and in some cases, replating pads that had been contaminated w
Electronics Forum | Tue May 10 15:44:24 EDT 2011 | davef
From your graph, we just don't see the the relationship between failures and relative humidity. Questions are: * What is the correlation between failures and RH? [We'd bet that the correlation between failures/RH and failures/temperature are 'similar