Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Fri Mar 29 17:58:21 EST 2002 | slthomas
We have a new assembly with bottom side components, and all the chip caps and resistors are 0603s. The dog boned shape of the caps necessitates a pretty big (and tall) dot to hold them still during placement, and when they get placed the dot squishe
Electronics Forum | Mon Jun 27 09:09:19 EDT 2005 | Bob R.
We've all been soldering Pb free parts for a couple decades. All your surface mount capacitors have probably had a Sn finish for years. Whenever one of our parts with a SnPb finish converts for Pb free we have the manufacturing site do a small buil
Electronics Forum | Mon Feb 20 13:29:44 EST 2006 | patrickbruneel
Great work Amol, Please keep us posted about the results of the x sectioning. I personally don't believe that the cracks are due to non-eutectic properties of SAC. Because the alloy is only 4�C off eutectic and when a solder joint exits the solder
Electronics Forum | Mon Apr 17 18:29:03 EDT 2006 | lit
There is learning on all brands requiring fine tuning the test parameters. The first point is not to allow defects to escape. Many brands can do a good job with preventing escapes. The struggle with all the brands becomes false calls. The companies r
Electronics Forum | Sun Feb 24 19:10:17 EST 2008 | larryd
Skill and experiance level of assemblers is critical. High skill and experiance with the type of assembly, print and BOM and hgihlighters. Day labor would be 5 to 10 components for each assembler, already prepped with pictures or drawings showing wh
Electronics Forum | Tue Mar 23 07:35:42 EDT 2010 | jooh
Since I'm new to the forum I probably ask previously answered questions (that I have not found) but I would be grateful if someone could clarify this for me. I'm in R&D at a company where we design low volume (1k-10k) fairly complex PCBAs for our pr
Electronics Forum | Thu Apr 08 19:32:52 EDT 1999 | Tom Reilly
FYI, Yes, it is true SMT Plus [ http://www.smtplus.com/ ]does not meet IPC 782 standards but is that the goal here or to meet IPC-A-610 standards for manufacturing? I agree that patterns do cause some problems if created to maximum IPC standards but
Electronics Forum | Wed Jul 21 20:52:52 EDT 1999 | Scott
| | I have pcb's in which i am experiencing warping. | | the boards are 12.8125" on a diagonal measurement. | | they are out approximatley .010". | | the boards are combination thru-hole,smt, they also have 3ounce copper.what is acceptable,and what i
Electronics Forum | Thu Jul 22 06:54:45 EDT 1999 | Earl Moon
| | | I have pcb's in which i am experiencing warping. | | | the boards are 12.8125" on a diagonal measurement. | | | they are out approximatley .010". | | | the boards are combination thru-hole,smt, they also have 3ounce copper.what is acceptable,an
EPTAC is an internationally recognized solder training and IPC certification corporation, giving professionals the skills to accelerate their careers, and businesses the talent to succeed.
Training Provider / Standards Setting / Certification
Longfellow Square, Bldg. II
Manchester, NH USA
Phone: 603-296-0887