Electronics Forum | Fri Dec 15 09:44:38 EST 2006 | mashmo
Hello I am a circuit board designer and just wanted to ask if anyone is seeing the need to alter footprints for ROHS assembly. I also wanted to make sure that I have this particular issue correct. If your BGA is lead free then used solder paste with
Electronics Forum | Wed Nov 08 15:22:54 EST 2006 | rgduval
Anyone have any experience with Displacement Soldering? We just came across a benchtop displacement soldering system, and I'm wondering how effective it might be for me. We're currently looking at a "best" solution for us right now for lead-free
Electronics Forum | Thu Jan 06 21:41:20 EST 2005 | James Khor
You can using Ersa IR550A Rework System. The unit was NOT using any hot air process. IR550A Rework System is worldwide the only system with a genuine closed loop control system. Which employs the current temperature at the component in order to regul
Electronics Forum | Wed Aug 27 14:38:20 EDT 2008 | rgduval
Does your paste provider recommend a TAL? For the leaded and lead-free pastes that we use, the manufacturer recommends 60 seconds above liquidous. I note that your profile shows the TAL as 30 seconds, which may not be sufficient. That said, tho
Electronics Forum | Tue Feb 16 21:29:18 EST 2010 | actioncontrols
I predict you will have no problems with your soldering. Remember that all plating is only a few microns thick and quickly washed away by the molten solder. We have used white tin, immersion gold, OSG, etc. for quite a while with leaded solder and
Electronics Forum | Thu Mar 13 16:32:25 EDT 2008 | dyoungquist
MyData PNP machines are good for high mix/low volume because change over time between jobs is lower than with many other PNP machines. They also handle parts on cut tape strips easily and you will have these with low volume runs. As for lead free o
Electronics Forum | Mon Nov 27 22:19:13 EST 2006 | ppcbs
800 degrees? Ouch! I find that every company that I do training for has at least one person that likes to go through one tip a day. The solution is tip tinning. Tell your operators to wipe the tip on a damp sponge often. Do not buy your sponges
Electronics Forum | Fri Jul 09 10:32:47 EDT 2010 | rafacadiz
Hi Sean, I have seen this issue with lead free component on Sn-Pb solder process, I don´t know if it´s your case. Some times, pins not reach the necessary T for solder due to lead free metalization and in other case due to a groud pad, with a big T d
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux