Electronics Forum | Tue Feb 19 22:57:38 EST 2008 | davef
Duno. What's the diameter of: * Finished connector lead * Finished through hole We reckon: Lead size plus ~0.25mm [0.010"] is normal.
Electronics Forum | Thu Nov 22 08:15:04 EST 2007 | davef
Paul: If your customer "resolders suspected IC lead(s), problem goes away" - It's not an 'black pad' issue. You need to improve the way you solder this product.
Electronics Forum | Mon Dec 10 17:43:28 EST 2007 | hussman
Looking for a thru hole part that you can solder a wire or leaded part to. I remember using them in the past - but the name escapes me. It had a forked end that the lead would fit into. Any help appreciated.
Electronics Forum | Thu Sep 25 04:57:51 EDT 2008 | fnorradd
Hi All, I was wondering if any of you have any ideas on what is the optimum angle for the conveyor to pass over the waves on a leaded wave machine ? Any input would be greatly appriciated. Regards Darron
Electronics Forum | Tue May 22 11:26:56 EDT 2012 | rway
Lead spacing is probably an issue here. It would be better if your lead pattern was staggered, like the RJ-45 to the right. It appears there may not be enough flux on this part of the pcb.
Electronics Forum | Wed Sep 09 17:22:42 EDT 2015 | jayrcomajig
Is there any electronic digital devices or other easiest ways to use to determine any unsoldered pins/leads besides some other normal inspections like using microscopes.
Electronics Forum | Thu Dec 19 03:02:48 EST 2019 | sssamw
I cannot see it's a gull wing lead, but also there's no solder under the lead except the side surface.
Electronics Forum | Wed May 11 20:38:18 EDT 2022 | donovan03608
The leads on the FPC are pre-tinned on both sides with SAC305. The receiving leads are AU. We do not experience any wetting issues that would suggest oxidation.
Electronics Forum | Wed May 11 20:41:53 EDT 2022 | donovan03608
The leads on the FPC are pre-tinned on both sides with SAC305. The receiving leads are AU. We coat all surfaces with Kester 979 no-clean flux dispensed via pen prior to initiating the hotbar cycle.
Electronics Forum | Wed May 11 20:43:42 EDT 2022 | donovan03608
The leads on the FPC are pre-tinned on both sides with SAC305. The receiving leads are AU. We do not experience any wetting issues that would suggest oxidation.