Electronics Forum | Fri Dec 29 08:14:19 EST 2006 | joey_dragon
Thank you for the quick reply! Actually, the "type B" I referred to applies to a flex cable that can be found in this page: http://www.tennrich.com/trtw/cabling_3.php It is a reverse Engineering project and, from what I can see, there is, indeed,
Electronics Forum | Fri Sep 18 11:23:32 EDT 2009 | isd_jwendell
I know nothing about Xbox specific rework, but have a lot of experience with PCB repairs. "...maybe think its a bad idea now not knowing what im doing" Don't get discouraged, it's a learning process. If it was that easy everyone would be doing it.
Electronics Forum | Mon Jun 14 13:47:54 EDT 1999 | Chrys Shea
| We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centre
Electronics Forum | Wed Jun 16 07:34:17 EDT 1999 | Glynn Technologies and Manufacturing
| | We are a medium sized PCB assy. house manufacturing about 2000 motherboards a day. There is a major problem we are facing at the wave soldering stage, i.e. warpage of the PCB. As soon as the PCB touches the wave it warps severely from the centr
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Thu Jun 17 22:10:48 EDT 1999 | Earl Moon
| | | Does anyone know where I can find a list of things to do to when troubleshooting issues during the wave solder process? | | | | | | for example: | | | | | | Solder Bridge | | | 1.verify amount of flux been aplied. | | | 2.verify turbulance on
Electronics Forum | Thu Aug 06 09:51:20 EDT 1998 | Bob Willis
This text may be of interest to any one with tin lead spots Guide to Solder Spots - A New Plague in Manufacture ? So what are solder spots ? They appear to be the next big problem in modern reflow assembly in fact in any process that involves solder
Electronics Forum | Tue Apr 17 13:33:00 EDT 2001 | Kris W
Howdy all! Nothin' up my sleeve!!! While attempting to reflow an RF antennae on std FR4, HASL coated, using no clean paste, in a Research Thermaflo 10, the part sometimes slides on one of the pads (as much as 0.125"). There is a slight amount of w
Electronics Forum | Tue Dec 07 16:34:54 EST 1999 | Russ
Wolfgang, I appreciate your continued feedback! The main reason that I shortened the Time Above Liquidous (TAL) was it appeared that I was burning off all of the flux from the paste. By shortening the TAL to 45 seconds and decreasing peak temp to
Electronics Forum | Sat Aug 14 01:21:29 EDT 1999 | Dean
| | Has anybody adopted the method of stencil printing with the board at a 45 degree angle to the squeegee blade? What are the benefits and drawbacks? I've heard you get better fine pitch results. | | | | TX | | Mark | | | I have used thetechni