Electronics Forum | Thu Oct 05 16:12:09 EDT 2006 | Mario Scalzo, SMT CPE
* Try 1.5C / sec from RT to 165C * Hot soak at 165-175C for up to 2 minutes (I'd start with 60 seconds flat soak.) * 60-90 seconds TAL (I's start with 60) * 230-240C Peak. Thanks, Mario
Electronics Forum | Fri Oct 06 15:43:33 EDT 2006 | Mario Scalzo, SMT CPE
What I usually do is keep the peak temperature about 5-10 deg C below the peak temperature of my lowest rated component, then set everything else up around that. Worse case scenario is to just extend the time above liquidus (TAL) in 5 second increme
Electronics Forum | Wed Mar 21 13:47:16 EDT 2012 | jax
To have an Operating Temp (Tool Classification) within your range, you might want to try. PB85 (Pb85/Sb10/Sn5) SMT is normally processed using Vapor Phase but can also be achieved with Nitrogen assisted Convection Reflow depending on size and compl
Electronics Forum | Sun Jan 30 21:56:05 EST 2000 | Paulvannan
We used Promosol Sn96.5/Ag 3.5 during our initial qualification for similar application. We could not achieve a shiny solder joint. Our changes to Sn95.5/Ag 4.5 does not improve the look. In order to confirm the reliability of the joint, I suggest yo
Electronics Forum | Wed Mar 21 13:16:11 EDT 2012 | grahamcooper22
What solder alloy are you using at the moment which is coming to the end of its limits ? Normally in general for safe operation of an alloy we don't like to recommend any operation temp that is higher then two thirds of the solders melt point, but th
Electronics Forum | Mon Jul 06 13:17:50 EDT 1998 | Upinder Singh
| | Hi all . | | Thanks to Ryan, Brian , Justin and Dave for the timely help earlier. | | I would appreciate if somebody could help me in the stated issue: | | I am trying to to place one thru hole 20 pin connector along with the SMT components by p
Electronics Forum | Thu Jul 14 16:07:16 EDT 2005 | saragorcos
Here is a link to a specific article about cleaning no-clean assemblies: http://www.residues.com/pdfs/Clean_No_Clean.pdf Our facility does a lot of contract cleaning and cleanliness testing for various companies around the world, and that study s
Electronics Forum | Tue Feb 28 13:46:28 EST 2006 | slthomas
Assuming you're using DOM and shelf life to determine what's good and what's not, you just have to know 1)the rate at which you use it up, 2) how much shelf life is left, and 3) the rate that it goes bad when not refrigerated. From that you can tel
Electronics Forum | Fri Oct 06 08:21:26 EDT 2006 | inds
Mario, what happens when there are components on the boards that are not rated to take temperature of 230-240 C Peak for a mixed assembly. I guess there are tons of sn/Pb components that have rated temp of 225-230 C.. So in guess you might want
Electronics Forum | Tue May 13 17:53:54 EDT 2014 | anvil1021
Hello Michel...this might be a bit of a battle finding the low thermal EMF material that you are looking for. The first one that comes to my mind is Bismuth Selenium Telluride, with either a nickel or cobalt doping agent. Silver went away from this