Electronics Forum | Sat Apr 30 10:37:25 EDT 2005 | Daniel
I think he did mentioned the board size in the inital thread: "265mm x 207mm pcb", but maybe it was not clear written. I have a question about rework and pre-heat: is it necessary to have the pre-heater to cover the whole board size, even if you onl
Electronics Forum | Sat Apr 30 13:56:31 EDT 2005 | steve
My experience with different size boards and pre-heaters. The perfect world (right?) you would saturate the complete pcb with bottom pre-heat. But it is difficult with repair and rework equipment, not to mention the expense and foot print of large pr
Electronics Forum | Mon May 09 10:52:29 EDT 2005 | patrickbruneel
Hannu, First and for all I have a problem with your question "tried and trusted" for the simple reason that you are going to change too lead-free. Ultrasonic soldering or welding is not new, as far as I know it is only used applying the ultrasonic
Electronics Forum | Sat May 14 17:25:20 EDT 2005 | fastek
"What can be done to create economical advantages over here is review the product flow and eliminate process steps with current existing technology. Process steps that can safely be eliminated are cleaning, visual inspection, post wave assembly etc.
Electronics Forum | Thu Jun 09 03:16:06 EDT 2005 | PSGill
I'm using Kester R520A Lead free solder paste. The flux % stated on the Certificate of Analysis(COA) when the product delivered to us is 10 %. The tolerance is 1%. But when i send the jar to an external lab to determine the flux % it is more than 11%
Electronics Forum | Sun Jun 12 12:10:14 EDT 2005 | Sven
Hi all, I agree with all the postings above, but I have a few ammendmets: (How is my english so far?) The purpose of the so called "local fiducials" was in the old days, when "board stretch" was a factor. At least people think that was a big matter..
Electronics Forum | Wed Jun 22 09:12:57 EDT 2005 | bsudak
Our manufacturing site has been struggling with soldering Alloy 42 TSOPs. Currently, we have to hand solder in one of our applications. Here are the particulars. Component: 54 leads, Sn plated, 400microinches +/-200. Process: Eutectic 63/37 Sn/Pb
Electronics Forum | Tue Jun 28 12:12:17 EDT 2005 | Paul
I'm with DaveF on this one. I think you'll be trying solve this one for a long time. Alloy42 just doesn't like to be soldered. What exactly is the issue? Lack of a toe fillets at on the cropped lead? There is no spec for a toe fillet other than to
Electronics Forum | Thu Jun 30 18:40:06 EDT 2005 | KEN
What your asking has many variables. 1. Material: SS vs. Cast Iron. Iron is thicker. Which SS? 316, 316L 2. Pump speeds, turbulence, hours of operation directly affect equipment life. 3. Things like scraping the pots, the tunnels, impelle
Electronics Forum | Fri Jul 08 09:57:31 EDT 2005 | fctassembly
Proy, Another issue is what exact formulation of SAC is used. Much of the SAC305 being used in Asia contains phosphorus, which is added in an attempt to reduce the heavy drossing that SAC305 produces. Phosphorus acts as a flux on steel so will increa