Electronics Forum | Tue Aug 31 12:01:26 EDT 2004 | russ
Kris, this practice has gone on for years. I have never heard of any problems associated with this. I have heard "grumblings" about tin lead parts being processed with lead free paste, but have seen or heard of no data to support. Russ
Electronics Forum | Tue Aug 31 19:17:43 EDT 2004 | russ
Now see Dave, now I have some good info on why it is "bad", This must be the lead enrichment I have heard about but never got any substantiated data or explanantion. I wonder how much weaker or less reliable these are. Is there any data that you k
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Fri Feb 11 16:58:24 EST 2005 | steve
I know this has been dealt with in the past but I couldn't dig up anything in the archives. If I'm soldering a 0402 lead free component with 63/37 solder is this a problem. Also lets take the opposite. If I'm soldering a lead bearing 0402 with lead f
Electronics Forum | Sun Feb 01 07:50:07 EST 2009 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Tue Feb 03 10:25:56 EST 2009 | milroy
Hi What is the surface finish you have? Following are true if you have HASL-LeadFree surface. I have had the same problem 3years ago and we did some micro-sectioning for further analysis, still the boards are functioning properly. But you have to
Electronics Forum | Fri Jan 30 18:24:09 EST 2009 | gsala
Buenas dias Jos�, It shoul not be a problem. We had situation like that when in the early 2006 the Lead Free fase in Pb fase out, no pbm on solder joints. Today, after about 3 years, those cards are stil working in the field without any defect. Reg
Electronics Forum | Fri Jan 30 15:11:50 EST 2009 | joseluis_amper
Dear Sir. Recently we had a problem in our production. We had pcbs with no RoHs (with solder Pb in pads) but we used paste Lead Free. I want to know if we will have problems in this solders in the future, because (perhaps)the solder will be broken, o
Electronics Forum | Tue Feb 03 03:35:30 EST 2009 | sachu_70
Hi Jose, such a process is possible, but you need to confirm that the PCB material has high Tg. In additon, you need to re-look solder paste printing parameters and make required changes in stencil apperture design for optimum solder volume. Just a
Electronics Forum | Mon Dec 12 14:04:33 EST 2005 | craigj
Hi All was wondering is there anything I should be aware of or look out for if using parts with SnBi (Pb free) lead plating with Sn/Pb/Ag solder paste? I was always lead to believe that mixng lead and bismuth caused problems or are the bismuth levels