Electronics Forum | Fri Oct 28 11:04:43 EDT 2005 | JW
We are planning to purchase a portable XRF unit to do our LF component testing. While we were running our first proto run of LF boards for a customer, we just happen to demo a XRF unit and found lead in a "certified Lead-free component"!!! Considerin
Electronics Forum | Fri Nov 04 15:02:29 EST 2005 | mo8080
SJ, Let me know if you need any assistacne in financing these machines. We are a bank-owned direct financing source and we specialize in electronic manufacturing equipment. Even if you have a financing company/bank that you always use it never hurts
Electronics Forum | Sat Dec 10 19:10:17 EST 2005 | mika
Most of the chip; res & caps are already lead-free or RoHS compliant and you most certainly already solder them in your regular leaded reflow process. However, there are a few more component packages except from BGA:s that are NOT backwards compatib
Electronics Forum | Thu Dec 01 00:34:15 EST 2005 | pyramus
Guy's another question, how about any recommendation what type of adhesive to use as underfill for BGA during lead free process? Currently, we are only using Loctite 3609 & 3515 as adhesive we use 3515 as BGA underfill during normal leaded process s
Electronics Forum | Tue Dec 13 06:56:27 EST 2005 | adanhn
Hi Steve, What I came up with for our Soltec Sigma 6621 is to make a stainless steel wave solder bath insert.The insert with all its components eg. impeller, Chipwave assy, pump shafts, main wave assy etc. I will send for plasma nitride coating.Afer
Electronics Forum | Thu Dec 22 04:34:47 EST 2005 | rlackey
11,000 parts? Easy life. We have 66,000 lines in stock & about 500,000 on the system. We've added extra fields on the database for every part number with ROHS status, MSL, PBT, & end termination info added. We've also had to create duplicate part
Electronics Forum | Thu Dec 29 11:43:46 EST 2005 | samir
CMiller, Thanks for the valuable info! We are in the midst of lead-free deployment and need to know good alloy choices at both wave and ERSA. I have heard the same things regarding SAC305's price for bar solder, but don't yet know what the process
Electronics Forum | Tue Jan 03 09:23:31 EST 2006 | Amol Kane
Hi all, Firstly, Wishing everyone a happy new year and a successful transition to RoHS (exempt entities please disregard the later part :-)) I am looking for a formal training institute/organization to train my operating personnel for lead-free hand
Electronics Forum | Fri Jan 20 09:17:59 EST 2006 | George
Hi "theSaint", We are using SN100C in our wave solder machine. As far as the solder itself, the wave process follows pretty much the same concept as leaded solder. You bring the assembly temp to 90 C or more before the actual wave. Sometimes for mul
Electronics Forum | Wed Feb 01 03:38:56 EST 2006 | Jose Luis
Hi all, I'm working in Military Production and then, We have an exception about RoHS (LEAD FREE), but, because we use "normal" components, in this moments, a lot of components have LEAD FREE terminations, and we think that after of 1st July, we wo'nt